用水热法制备TiO2纳米材料,并对TiO2表面进行修饰.通过场发射扫描电子显微镜(SEM)和光电子能谱(XPS)对材料表面结构和成分进行分析.结果表明TiO2薄膜表面包覆了一层粒径较大的SrCO3颗粒,整个电极表面呈现均匀的多孔结构.使用电化学工作站对电池进行光电性能分析和EIS测试,由Ⅰ-Ⅴ曲线的结果可得,修饰后的电极性能更优越,短路电流提高了39.9％,光电转化效率提高了38.3％.由电化学阻抗谱(EIS)测试结果可以看出,修饰后TiO2/dye/电解质的界面阻抗大于修饰前,说明包覆层在一定程度上起到了阻碍电荷复合的作用,从而减小了暗电流.
参考文献
| [1] | Michael Gratzel .Dye-sensitized solar cells[J].Journal of photochemistry and photobiology, C. Photochemistry reviews,2003(2):145-153. |
| [2] | Gratzel M .Solar energy conversion by dye-sensitized photovoltaic cells[J].Inorganic Chemistry: A Research Journal that Includes Bioinorganic, Catalytic, Organometallic, Solid-State, and Synthetic Chemistry and Reaction Dynamics,2005(20):6841-6851. |
| [3] | 孙惠成,罗艳红,李冬梅,孟庆波.染料敏化太阳能电池基础研究及产业化新进展[J].硅酸盐学报,2011(07):1045-1052. |
| [4] | Aswani Yella;Hsuan-Wei Lee;Hoi Nok Tsao;Chenyi Yi;Aravind Kumar Chandiran;Khaja Nazeeruddin;Eric Wei-Guang Diau;Chen-Yu Yeh;Shaik M Zakeeruddin;Michael Gratzel .Porphyrin-Sensitized Solar Cells with Cobalt (Ⅱ/Ⅲ)-Based Redox Electrolyte Exceed 12 Percent Efficiency[J].Science,2011(Nov.4 TN.6056):629-634. |
| [5] | 吴季怀,郝三存,林建明,黄昀昉.染料敏化TiO2纳晶太阳能电池研究进展[J].华侨大学学报(自然科学版),2003(04):335-344. |
| [6] | 敏世雄,彭晓霞,佘世雄,佟永纯,白洁,苏碧桃.过渡金属离子掺杂对TiO2纳米尺寸及其相结构的影响[J].化工新型材料,2006(03):46-48. |
| [7] | Deng HH.;Zhang H.;Lu ZH. .Dye-sensitized anatase titanium dioxide nanocrystalline with (001) preferred orientation induced by Langmuir-Blodgett monolayer[J].Chemical Physics Letters,2002(5-6):509-514. |
| [8] | 庄东填,林红,李鑫,李建保.染料敏化太阳能电池中TiO2光阳极的包覆效果[J].硅酸盐学报,2010(09):1848-1851. |
| [9] | 徐雪青,徐刚.CdSe量子点敏化纳米二氧化钛太阳电池的电化学交流阻抗谱[J].中国科学（化学）,2011(01):37-43. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%