Research work and recent progress made toward the industrial applications of the Ni_3Al in CISRI are discussed in present paper. The development of a Ni_3Al base alloy named MX-246 hardened by carbides and fine dispersion of disordered γ is summaried. This alloy,with higher peak temperature of yield strength and higher strain hardening rate than alloyIC-218,has been successfully used as the material of rolling guider at elevated temperatures and in wear conditions. The Ni3Al base alloy of GH264 has been made into welding electrodes by horizontal continuous casting process, and recently successfully surfacing welded on hydraulic blades as cavitation erosion resistance material. The process of remelting Ni3Al base alloy in air was also developed. The processes of producing welding electrodes and remelting in air set the base of industrial applications of Ni3Al in welding, repairing and casting in mass production and into components of large size. Another application of the compound, manufacturing the jet engine rivets used at about 1300℃ , can be attributed to its excellent oxidation resistance and still keeping high strength up to the melting point.
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | |
| [5] | |
| [6] | |
| [7] | |
| [8] | |
| [9] | |
| [10] | |
| [11] | |
| [12] | SikkaVK,MavityJT,AndersonK．MaterSciEng,1992:Al53:7122DimidukDM,MiracleDB,WardCH．MaterSciTechnol,1992:8:3673NakaS,ThomasM,KhanT．MaterSciTechnol,1992 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%