The ultrasonic peening of weld toes in ultra-fine grain steel was applied to enhance the fatigue behavior. The test results show that the ultrasonic treatment remarkably shifts the S-N curve to the right. The FAT (fatigue strength at 106 cycles) is increased by 66 %. The fatigue life at Δσ=200 MPa is extended by 58 times. The mechanism of fatigue strength improvement by ultrasonic treatment was studied. It is shown that two mechanisms improve the fatigue strength of welded joint by ultrasonic treatment: one is the decrease of the stress concentration ratio at weld toes, and the other is the building-up of a compressive residual stress at the weld.
参考文献
| [1] | Weng Yu-qing.Development of HSLA Steels in China atTurn of Century[A].Beijing:Metallurgical Ind-ustry Press,2000:3-10. |
| [2] | LIU Qing-you.Controlled Rolling of Ultra Fine Ferrite in Microalloyed Steels[A].北京:冶金工业出版社,2000:233-237. |
| [3] | Akihiko OHTA;Naoyuki SUZUKI;Yoshio MAEDA.Fatigue Strength Improvement by Inducing Compressive Residual Stress Using Low Transformation Temperature Welding Material[A].NRIM,2001:238-239. |
| [4] | Huo Li-xing.Investigation on Improving Fatigue Properties of Welded Joints by Ultrasonic Peening Method[A].PohangKorea,2000 |
| [5] | HUO Li-xing.Fracture Behavior of Welded Structures[M].北京:机械工业出版社,2000 |
| [6] | Tang Mu-rao.Measuring Techniques for Welds[M].北京:机械工业出版社,1988 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%