热物理模拟获得了铸态AZ80镁合金热压缩真应力-应变曲线,以此作为计算动态再结晶体积分数演变的底层数据.通过求解流动应力的双曲正弦表征模型,获得了本构模型与动态再结晶激活能等重要参数.分析峰值应力出现之前与之后的硬化曲线,识别了真应力-应变曲线所隐含的关键应变点:临界应变,峰值应变及最大软化速率应变.进一步引入表征晶体动力学的修正的Avrami方程,设计一个无量纲的中间变数Z/A,全面表征了动态再结晶体积分数、温度、应变速率及应变量之间的动态耦合作用.分析结果表明,应变量达到一定时才会诱发动态再结晶.随着应变的增加,动态再结晶的体积分数将逐渐增至100%增大应变速率或降低变形温度都会抑制动态再结晶的发生.
参考文献
[1] | Zhou H T;Li Q B;Zhao Z K et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2010,527(7-8):2022-2026. |
[2] | Al-Samman T;Gottstein G .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2008,490(1-2):411-420. |
[3] | Bacroix B;Driver J H;Gall R L et al.[J].Materials Science Forum,2004,467-470:531-536. |
[4] | Dehghan-Manshadi A;Barnett MR;Hodgson PD .Recrystallization in AISI 304 austenitic stainless steel during and after hot deformation[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):664-672. |
[5] | Ueki M;Horie S;Nakamura T .[J].Scripta Metallurgica,1985,19(04):547-549. |
[6] | Quan G Z;Liu K W;Zhou J .[J].Transactions of Nonferrous Metals Society of China,2009,19(z3):S537-S541. |
[7] | Yue, CX;Zhang, LW;Liao, SL;Pei, JB;Gao, HJ;Jia, YW;Lian, XJ .Research on the dynamic recrystallization behavior of GCr15 steel[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2009(1/2):177-181. |
[8] | Ji G L;Li F G;Li Q H et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2010,527(1-2):2350-2355. |
[9] | S.F.MEDINA;C.A.HERNANDEZ .THE INFLUENCE OF CHEMICAL COMPOSITION ON PEAK STRAIN OF DEFORMED AUSTENITE IN LOW ALLOY AND MICROALLOYED STEELS[J].Acta materialia,1996(1):149-154. |
[10] | S.F.MEDINA;C.A.HERNANDEZ .MODELLING OF THE DYNAMIC RECRYSTALLIZATION OF AUSTENITE IN LOW ALLOY AND MICROALLOYED STEELS[J].Acta materialia,1996(1):165-171. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%