对医用Ti-15Mo-3Nb合金熔炼、锻造、热处理过程中发生的组织和性能的变化进行的研究。并结合相图与JMatPro-4.0软件的模拟结果来确定再结晶退火温度。结果表明,铸态和锻态下的Ti-15Mo-3Nb医用β钛合金的组织和性能很不稳定,不适合直接用于临床。该合金经再结晶退火或固溶时效处理后,合金组织均被细化,抗压强度提高,且再结晶退火后,该合金的压缩弹性模量为19.4 GPa,与人体密质骨的（17-18.9GPa）最为接近,更能满足其作为植入体对生物力学适应性的要求。
Microstructure and properties of Ti-15Mo-3Nb alloy in different treatment conditions were studied.The recrystallization annealing temperature of the alloy was determined according to phase diagrams and the simulation result by JMatPro-4.0 soft.The results show that the microstructure and properties of as-cast and forged Ti-15Mo-3Nb alloy are unstable.The microstructure of the alloy after recrystallization annealing treatment or solution and aging treatment is refined.At the same time,their compressive strength increases greatly.The compressive elastic modulus of the alloy after recrystallization annealing treatment is 19.4 GPa nearly to that(17-18.9 GPa) of human body compact bone,which will make it more satisfactory in biomechanical adaptability as surgery implants.
参考文献
| [1] | 阮建明;邹俭鹏;黄伯云.生物材料学[M].北京:科学出版社,2004 |
| [2] | Rack HJ;Qazi JI .Titanium alloys for biomedical applications[J].Materials science & engineering, C. Biomimetic and supramolecular systems,2006(8):1269-1277. |
| [3] | ZHAO Jie;DUAN Hong-tao;LI Hai-tao .Microstructure and mechanical properties of biomedical Ti-27Nb-SZr alloy with low elastic modulus[J].Rare Metal Materials and Engineering,2010,39(10):1707-1710. |
| [4] | Eisenbarth E;Velten D;Muller M;Thull R;Breme J .Biocompatibility of beta-stabilizing elements of titanium alloys.[J].Biomaterials,2004(26):5705-5713. |
| [5] | Laheurte P;Prima F;Eberhardt A;Gloriant T;Wary M;Patoor E .Mechanical properties of low modulus beta titanium alloys designed from the electronic approach.[J].Journal of the mechanical behavior of biomedical materials,2010(8):565-573. |
| [6] | 戚玉敏,李勇,崔春翔,刘双进,梁建平,赵立臣.固溶处理对医用Ti-15Mo合金显微组织及性能的影响[J].金属热处理,2008(03):83-85. |
| [7] | 候增寿;卢光熙.金属学原理[M].上海:上海科学技术出版社,1993 |
| [8] | E A 鲍利索娃;等;陈石卿.钛合金金相学[M].北京:国防工业出版社,1986 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%