通过模拟渗碳试验,研究了Nb对齿轮钢20CrMnTi晶粒粗化行为的影响.结果表明,由于析出含Nb析出相,Nb能显著提高在模拟渗碳过程中的晶粒粗化温度.晶粒粗化温度由析出相的体积分数和析出相的尺寸决定.当模拟渗碳温度较低时,时间对析出相尺寸影响不明显;当渗碳温度较高时,延长时间析出相明显粗化.因此,对于Nb含量较低的试样,1h和6h模拟渗碳的晶粒粗化温度接近;而对于Nb含量较高的试样6h模拟渗碳的晶粒粗化温度比1h的低.
参考文献
| [1] | Davis J R.Surface Hardening of Steels:Understanding the Basics[M].Ohio:ASM International,2002 |
| [2] | D. K. Matlock;J. G. Speer .Microalloying concepts and application in long products[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2009(9):1118-1125. |
| [3] | M. Kubota;T. Ochi .Development of Anti-Coarsening Steel for Carburizing[J].Materials Science Forum,2007(Pt.5):4855-4860. |
| [4] | K. A. ALOGAB;D. K. MATLOCK;J. G. SPEER;H. J. KLEEBE .The Effects of Heating Rate on Austenite Grain Growth in a Ti-modified SAE 8620 Steel with Controlled Niobium Additions[J].ISIJ International,2007(7):1034-1041. |
| [5] | Alogab K A;Matlock D K;Speer J G et al.The influence of niobium microalloying on austenite grain goarsening behavior of Ti-modified SAE 8620 steel[J].ISIJ International,2007,47(02):307-316. |
| [6] | 杨林,邵亮,乔兵,杜彩霞.含Nb齿轮钢晶粒度研究[J].汽车工艺与材料,2004(07):5-6. |
| [7] | 马莉,王毛球,董瀚.微合金化渗碳齿轮钢的研究进展[J].特殊钢,2008(04):28-30. |
| [8] | 马莉,王毛球,徐香秋,王连海,赵亚平,董瀚.铌硼微合金化齿轮钢的晶粒尺寸及淬透性[J].材料热处理学报,2009(05):74-78,91. |
| [9] | 王毛球,时捷,惠卫军,董瀚.V-Nb微合金化重载齿轮钢的组织和力学性能[J].材料热处理学报,2007(z1):18-21. |
| [10] | 杨延辉,王毛球,王春芳,董瀚,陈敬超.钛铌微合金化齿轮钢的奥氏体晶粒长大研究[J].钢铁研究学报,2012(12):32-36. |
| [11] | 刘燕,王毛球,樊刚,时捷,惠卫军,董瀚.含铌齿轮钢的晶粒长大动力学[J].钢铁研究学报,2008(11):37-42. |
| [12] | 余永宁.金属学原理[M].北京:冶金工业出版社,2000 |
| [13] | 雍岐龙;马鸣图;吴宝榕.微合金钢-物理和力学冶金[M].北京:机械工业出版社,1989 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%