利用了三点弯曲法研究了碳纳米管膜压阻效应.研究中所用的碳纳米管是用化学气相沉积法合成的.实验结果表明,碘掺杂和未掺杂的碳纳米管膜的压阻因子在500微形变和室温下分别为350和65,超过了单晶硅和多晶硅的压阻因子.同时还发现化学处理还能进一步增强碳纳米管膜的压阻效应.碘掺杂碳纳米管膜的压阻效应也许是由于在形变时带隙变化所致,而未掺杂碳纳米管压阻效应主要是由管之间接触电阻变化引起的.碳纳米管压阻效应可用于旋转速度的测量.
参考文献
| [1] | Iijima S .Helical micotubes of graphitic Carbon[J].Nature,1991,358:56. |
| [2] | Martel R.;Shea HR.;Hertel T.;Avouris P.;Schmidt T. .Single- and multi-wall carbon nanotube field-effect transistors[J].Applied physics letters,1998(17):2447-2449. |
| [3] | Toms S J;Verschueren A R M;Decker C et al.Roomtemperature transistor based a single Carbon nanotube[J].Nature,1998,393:49. |
| [4] | Bathtold A;Hoaley D;Nakanishi T et al.logic circuits with Carbon nanotube transistor[J].Science,2001,294:1317. |
| [5] | 李勇,王万录,廖克俊,胡陈果,黄智,冯庆.碳纳米管膜的压阻效应[J].科学通报,2003(01):26-28. |
| [6] | 万步勇,王万录,廖克俊,吴子华,王永田,余鹏,孙鹏.多壁碳纳米管气敏性质的研究[J].真空科学与技术学报,2003(05):323-327. |
| [7] | 高永刚,施兴华,赵亚溥.碳纳米管的力学行为[J].机械强度,2001(04):402-412. |
| [8] | Tombler T W;Zhou C W;Alexseyev L et al.Reverible electromechonical characteristics of carbon nanotubes under probe manipulation[J].Nature,2000,405:769. |
| [9] | Wang Wan-Lu;Liao Ke-Jun;Li Yong;Wang Yong-Tian .Piezoresistive Effect of Doped carbon Nanotube/Cellulose Films[J].Chinese physics letters,2003(9):1544-1547. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%