采用Gleeble-3500热模拟机单道次压缩变形试验,研究了硼对460B钢的连续冷却转变过程及转变产物组织性能的影响规律.结果表明:硼元素的加入可以使460B钢在3℃/s的冷却速度下发生贝氏体相变,且与不含硼试样相比,在相同的冷速下所获得的板条状贝氏体组织更细小,且在低冷速(0.1、0.3、0.5℃/s)下晶粒略粗大但硬度偏高;硼元素的加入明显使460B钢的动态CCT曲线右移,抑制了奥氏体向铁素体和珠光体的转变,明显增加了钢的淬透性,降低了奥氏体向马氏体转变的临界冷却速度,同时也降低了460B钢的A c3、A cl、An、A r1和Ms点的温度.
参考文献
| [1] | 胡新华,完卫国,张建平.460MPa级高强度含钒钢筋的生产试制和性能[J].钢铁,2005(02):47-50,58. |
| [2] | 贺信莱;褚幼义;于宗森 .硼在钢中的分布[J].金属学报,1977,13(04):235. |
| [3] | 王宇平 .薄板坯连铸连轧硼微合金化低碳钢边裂原因的研究[D].昆明:昆明理工大学,2008. |
| [4] | Nakasato F;Takahashi M .Effect of B,Ti and N on the Hardonability of Boron-Treated Steel for Heavy Machinery[J].Metals and Technology,1979,3:102. |
| [5] | Arno B;Hendrik J .Theoretical and Experimental Damage Prediction in Cold and Semi-Hot Bulk Forming of Ducile Steels[J].Steel Research International,2005,76(2/3):210. |
| [6] | Chown, LH;Cornish, LA .Investigation of hot ductility in Al-killed boron steels[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1/2):263-275. |
| [7] | Y. R. Cho;B. S. Seong .Effect of Boron Addition on the Microstructure and Mechanical Properties of Low-carbon Steels[J].AISE Steel Technology,2004(5):46-51. |
| [8] | Lo'pez-Chipres E;Meji'a I;Maldonado C et al.Hot Ductility Behavior of Boron Microalloyed Steels[J].Material Science and Engineering,2007,460-461:464. |
| [9] | 范鼎东,张建平,肖丽俊,郭亚东.硼微合金化对SPHC钢组织、析出物以及屈服强度的影响[J].钢铁,2006(09):60-64. |
| [10] | 郭亚东,肖丽俊,仇圣桃,颜慧成,朱苗勇.TSCR工艺生产SPHC板过程硼微合金化对AlN、MnS析出的影响[J].钢铁研究学报,2007(07):24-27. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%