Ti50.6Pda0Ni19.4 and Ti51Pd2sNi21 (Ce) alloys have been prepared under various temperatures for long time annealing. Differential scanning calorimetery (DSC), X-ray diffraction (XRD) and tensile test were employed to investigate the phase transformation behavior and superelasticity of the alloys. It has been found that the phase transformation temperature of Ti50.6Pd30Ni19.4 is about 40℃ higher than that of Ti51Pd28Ni21(Ce), and do not change much with different annealed temperature. Obvious superelasticity is retained in Ti50.6Pd30Ni19.4 alloy annealed at 400℃ for 18 h, and annealing at higher temperature shows a deterioration of this property. The Ce addition in Ti51Pd28Ni21 alloy significantly delays recrystallization, increases yied strength and elastic modulus, but the superelasticity is poor.
参考文献
[1] | K Otsuka;K Oda;Y Ueno;M Piao .[J].Scripta Metallurgica et Materialia,1993,29:1355. |
[2] | D Golberg;Y Xu;Y Murakami;S Morito and K Otsuka .[J].Intermetallics,1995,3:35. |
[3] | S. Shimizu .Improvement of shape memory characteristics by precipitation-hardening of Ti-Pd-Ni alloys[J].Materials Letters,1998(1/2):23-29. |
[4] | D. Golberg;Y. Xu;Y. Murakami .High-temperature shape memory effect in Ti_(50)Pd_(50-x)Ni_x (x= 10, 15, 20) alloys[J].Materials Letters,1995(5/6):241-248. |
[5] | D Golberg;Y Xu;Y Murakami;S Morito, K Otsuka, T Ueki and H Horikawa .[J].Scripta Metallurgica et Materialia,1994,30:1349. |
[6] | W Cai;K Otsuka;M Asai .[J].Materials Transactions,1999,40:895. |
[7] | Y Xu;S Shimizu;Y Suzuki;K Otsuka, T Ueki and K Mitose .[J].Acta Materialia,1997,45:1503. |
[8] | Q C Tian;J S Wu .[J].Materials Science and Engineering A,2002,325:249. |
[9] | Y C Lo;S K Wu .[J].Scripta Metallurgica et Materialia,1992,27:1097. |
[10] | N M Matveeva;Yu K Kovneristyi .[J].Journal of Physics,1982,43:C4-249. |
[11] | Q C Tian;J S Wu .[J].Zeitschrift fur Metallkunde,2001,5:436. |
[12] | C. Y. Chung;C. Y. Xie;T. Y. Hsu .Effect of rare earth element Nd on the ductility and fracture behavior of a Ni-rich NiAl alloy[J].Scripta materialia,1997(1):99-102. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%