采用Gleeble-1500热模拟试验机研究15%SiC颗粒增强铝基复合材料在温度为713～773 K、应变速率为0.001～1 s-1的热变形行为,并建立热变形本构方程;同时采用Quantiment-500型自动图形分析仪测量该材料的动态再结晶晶粒尺寸.在研究中,以试验数据为基础,建立和((/((-(曲线,从而进一步获得动态再结晶的临界应变和稳态应变,并通过试验数据的回归分析,建立动态再结晶的临界应变模型和稳态应变模型,并在此基础上,获得所研究材料的动态再结晶图.
参考文献
| [1] | Ganesan G;Raghukandan K;Karthikeyan R .[J].Materials Science and Engineering A,2004,369(1-2):230. |
| [2] | Ganesan G;Raghukandan K;Karthikeyan R .[J].Journal of Materials Processing Technology,2005,166(03):423. |
| [3] | Ramanathan S;Karthikeyan R;Ganasen G .[J].Materials Science and Engineering A,2006,441(1-2):321. |
| [4] | Ramanathan S;Karthikeyan R;Gupta Manoj .[J].Journal of Materials Processing Technology,2007,183(1/5):104. |
| [5] | McQueen HJ.;Ryan ND. .Constitutive analysis in hot working[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1-2 Special Issue SI):43-63. |
| [6] | 李淼泉,李晓丽,龙丽,许广兴,于浩,迟彩楼,温国华.TA15合金的热变形行为及加工图[J].稀有金属材料与工程,2006(09):1354-1358. |
| [7] | Poliak E I;Jonas J J .[J].Acta Materialia,1996,44(01):127. |
| [8] | 刘建涛,张义文,陶宇,刘国权,胡本芙.FGH96合金动态再结晶行为的研究[J].材料热处理学报,2006(05):46-50. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%