为探索适于中温条件下使用的固体氧化物燃料电池的阴极材料,用固相反应法制备了Gd0.8Sr0.2CoO3(GSC)阴极粉体,用X射线衍射考察了GSC的成相温度.采用丝网印刷法将GSC-(Sm2O3)0.1(CeO2)0.8(SDC)沉积在SDC电解质圆片上,制成对称阴极,在不同温度下烧结.用交流阻抗谱从500～750℃测量了GSC-SDC复合阴极和SDC电解质之间的界面电阻.结果表明,GSC-SDC复合阴极的界面电阻比GSC阴极降低了3～5倍;750℃时,GSC-SDC阴极的界面电阻仅为0.15Ω·cm2.
参考文献
| [1] | Minh N Q .[J].Journal of the American Ceramic Society,1993,76:563. |
| [2] | Kenjo T;Nishiya M .[J].Solid State Ionics,1992,57:295. |
| [3] | Horita T.;Sakai N.;Yokokawa H.;Kawada T.;Kato T.;Yamaji K. .Oxygen reduction sites and diffusion paths at La0.9Sr0.1MnO3-x/yttria-stabilized zirconia interface for different cathodic overvoltages by secondary-ion mass spectrometry[J].Solid state ionics,2000(1/2):55-65. |
| [4] | Perry Murray E;Barnett S A .[J].Solid State Ionics,2001,143:265-273. |
| [5] | Lankhorst H M R;Bouwmeester H J M .[J].Journal of the Electrochemical Society,1998,144:1261. |
| [6] | Steele BCH. .Appraisal of Ce1-yGdyO2-y/2 electrolytes for IT-SOFC operation at 500 degrees C[J].Solid state ionics,2000(1/4):95-110. |
| [7] | Murray EP.;Sever MJ.;Barnett SA. .Electrochemical performance of (La,Sr)(Co,Fe)O-3-(Ce,Gd)O-3 composite cathodes[J].Solid state ionics,2002(1/2):27-34. |
| [8] | Xia CR.;Rauch W.;Chen FL.;Liu ML. .Sm0.5Sr0.5CoO3 cathodes for low-temperature SOFCs[J].Solid state ionics,2002(1/2):11-19. |
| [9] | Phillips M B;Sammes N M;Yamamoto O .[J].Solid State Ionics,1999,123:131-138. |
| [10] | Zeng Y.;Swartz SL.;Lin YS. .Perovskite-type ceramic membrane: synthesis, oxygen permeation and membrane reactor performance for oxidative coupling of methane[J].Journal of Membrane Science,1998(1):87-98. |
| [11] | Bell RJ.;Drennan J.;Millar GJ. .Influence of synthesis route on the catalytic properties of La1-xSrxMnO3[J].Solid state ionics,2000(3/4):211-220. |
| [12] | Zha S W;Xia C R;Meng G Y .[J].Journal of Power Sources,2003,115:44-48. |
| [13] | Jiang S P;Love J G;Ramprakash Y .[J].Journal of Power Sources,2002,110:201-208. |
| [14] | Hayashi K;Hosokawa M;Yoshida T;Ohya Y;Takahashi Y;Yamamoto O;Minoura H;Gifu Univ Fac Engn Dept Chem Gifu 50111 Japan.;Mie Univ Fac Engn Dept Chem Tsu Mie 514 Japan. .La1-xSrxMnO3-YSZ composite film electrodes prepared by metal-organic decomposition for solid oxide fuel cells[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,1997(3):239-242. |
| [15] | Steele BCH. .Materials for IT-SOFC stacks 35 years R&D: the inevitability of gradualness? [Review][J].Solid state ionics,2000(1/2):3-20. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%