采用低温固相反应法结合放电等离子体烧结法(SPS)合成了Mg2Si1-xSnx(0≤x≤1)三元化合物,研究了Sn固溶量对化合物热电性能的影响.结果表明,随Sn含量增加,材料电导率增加,Seebeck系数减小;材料晶格热导率先减小后增加,x=0.4时化合物晶格热导率最低,同时固溶体化合物的晶格热导率远低于Mg2Si和Mg2Sn二元化合物的晶格热导率,在室温附近Mg2Si1-xSnx固溶体化合物的晶格热导率均约为Mg2Si的1/3和Mg2Sn的1/2;Mg2Si0.8Sn0.2化合物具有最好的热电性能,在640K获得最大热电优值0.16.
参考文献
| [1] | Zaitsev V K;Fedorov M I;Eremin I S et al.[J].Chap,2005,29:1-11. |
| [2] | Zaitsev V K;Fedorov M I;Gurieva E A et al.[J].Physical Review B:Condensed Matter,2006,74:045207. |
| [3] | Isoda Y;Nagai T;Fujiu H.[A].Bajing,2006:406-500. |
| [4] | Zhang Q;Zhu T J;Zhao X B et al.[J].Applied Physics Letters,2008,93:102109. |
| [5] | Yoshinaga M;Iida T;Noda M;Endo I;Takanashi Y .Bulk crystal growthOf Mg2Si by the vertical Bridgman method[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2004(1):86-89. |
| [6] | Jung IH;Kang DH;Park WJ;Kim NJ;Ahn S .Thermodynamic modeling of the Mg-Si-Sn system[J].Calphad: Computer Coupling of Phase Diagrams and Thermochemistry,2007(2):192-200. |
| [7] | Nikitin E N;Tkalenko E N;Zaitsev V K et al.[J].Izv Akad Nauk SSSR,Neorg Mater,1963,4 |
| [8] | Zhang Q;Zhu T J;Zhao X B et al.[J].Physica Scripta,2007,T129:123-126. |
| [9] | Song RB;Aizawa T;Sun JQ .Synthesis of Mg2Si1-xSnx solid solutions as thermoelectric materials by bulk mechanical alloying and hot pressing[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2007(2/3):111-117. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%