The low carbon dual phase structure was cold de formed first,then was tempered at 200 to 600℃.The variation in strength and ductility during tempering of the steel was investigated.It was found that a fter the de formed dual phase structure was tempered at 200 to 600℃, with the increase in the tempering temperature the tensile strength decreases rapidly;the lotal elongation remains constant at 200 to 500℃ but began to rise dramatically at a critical temperature between 500 and 600℃.However,when the non-deformed dual phase structure was tempered at the same temperature range,the tensile strength decreases and the total elongation increases continuously with the increase of temperature.It was demonstrated from TEM analysis that precipitating carbides density along the boundaries ofmartensite lath and the recrystallized grains are responsible for the tempering response ofthe de formed dual phase structure.
参考文献
| [1] | |
| [2] | SpeichGR,SchwoebleAJ,HuffmanGP．MetallTrans,1983:14A:10792ChangPH．MetallTrans,1984:15A:733ChangPH．MetallTrans,1984:15A:6714ShenHP．MetalTreatment,1987:11:53(inChinese)5LeiTC,ShenHP．inMcQueenHJetal(Eds),StrengthofMetalsandAlloys,TheInstituteofMetals,London,1985 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%