从稀土化合物的制备、性能出发,比较并讨论了稀土纳米粉体材料的各种制备方法,荧光、催化和光伏等物理特性,并对今后的研究重点和发展前景进行了展望.
参考文献
[1] | 肖军 等.[J].应用化学,1992,9(05):104. |
[2] | 肖军,洪广言.Effect of Rare Earth on the Corrosion-Resisting Performance of Zinc-Based Alloy Coatings[J].JOURNAL OF RARE EARTHS,1993(01):32. |
[3] | 董相廷 等.[J].材料科学与工艺,1994,2(01):11. |
[4] | 于德才 等.[J].化学学报,1994,52:784. |
[5] | 董相廷 等.[J].稀有金属,1996,20(01):6. |
[6] | 董相廷,曲晓刚,洪广言,于德才,陆天虹,倪嘉缵.CeO2纳米晶的制备及其在电化学上的应用[J].科学通报,1996(09):847-850. |
[7] | 董相廷,刘桂霞,孙晶,李建利,刘景和,洪广言.Yb2O3纳米晶的制备及其若干性质的研究[J].稀有金属材料与工程,2001(01):73-76. |
[8] | 林晓敏,李莉萍,罗微,苏文辉.纳米晶固溶体Ce0.8Nd0.2O2-δ的合成与表征[J].高等学校化学学报,2001(04):531-534. |
[9] | Matijevic E;Hsu WP .[J].Journal of Colloid and Interface Science,1987,118(02):506. |
[10] | Sordelet D;Akinc M .[J].Journal of Colloid and Interface Science,1988,122(01):47. |
[11] | 洪广言 等.[J].无机材料学报,1996,11(03):542. |
[12] | 加藤昭夫;森满由紀子 .[J].日化,1984,23:800. |
[13] | Blendell J E;Bowen H K;Coble R L .[J].American Ceramic Society Bulletin,1984,63(06):797. |
[14] | SHI J L;Gao J H;Lin Z X.[J].Solid State Ionics,1989:537. |
[15] | 日館隆明;津九問孝次 .[J].陶瓷,1982,17:816. |
[16] | Mazdiyashi .[J].Ceramics International,1982,8(08):42. |
[17] | 尾崎羲治.[J].日本的科学与技术,1985(01):21. |
[18] | 景晓燕 等.[J].应用化学,1990,7(02):92. |
[19] | [Z].C.A. 102,151527c |
[20] | Wenzhong W;Geng Y;Yitai Q A .[J].Journal of the American Chemical Society,1999,121(16):4062. |
[21] | Lee M.H.;Oh S.G. .Characterization of Eu-Doped Y_2O_3 Nanoparticles Prepared in Nonionic Reverse Microemulsions in Relation to Their Application for Field Emission Display[J].Journal of the Electrochemical Society,2000(8):3139-3142. |
[22] | Briuker C J.Sol-Gel Science[M].Academic Press INC,1990 |
[23] | Dislich H Angew .[J].Chem Iterm Edit,1971,10(06):363. |
[24] | Weston T B;Webster A H;Menamara V M .[J].Journal of Can Ceram Soc,1967,36:15. |
[25] | Blasse G;Grabmaier B C.Lnminescent Materials[M].Springer-Verlag,1994 |
[26] | Williams D K;Bihari B;Tissue B M .[J].Journal of Physical Chemistry B,1998,102:916. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%