研究了室温下绿硫菌培养液中低碳钢的腐蚀电化学行为.结果表明,绿硫菌在50 h的潜伏期后发展迅速,并在192 h达到最大值,然后进入衰亡期.溶液中绿硫菌新陈代谢生理活动同步引起硫离子浓度快速下降和pH值快速增加.pH值增加会直接导致阳极溶解速度下降,甚至发生钝化;硫离子浓度下降也降低溶液的腐蚀性.溶液环境化学状态的变化也同步导致碳钢的腐蚀过程减慢.可以证明,绿硫菌是一种通过改变溶液化学性质来抑制金属腐蚀过程的微生物.
参考文献
| [1] | Moiseeva L S,Kondrova O V.Biocorrosion of oil and gas field equipment and chemical methods for Its suppression I[J].Prot.Met.,2005,41 (4):385. |
| [2] | 张颖,郑家燊.碳钢在H2S盐水体系中的腐蚀及保护[J].材料保护,1999(3):32. |
| [3] | 何生厚.高含硫化氢和二氧化碳天然气田开发工程技术[M].北京:中国石化出版社,2008. |
| [4] | 刘如林,刁虎欣.光合细菌及其应用[M].北京:中国农业科技出版社,1991,12:4. |
| [5] | Henshaw P F,Bewtra J K,Biswas N.Hydrogen sulphite conversion to elemental sulphur in a suspended-growth continuous stirred tank reactor using chlorobium limicola[J].Water Bes.,1998,32:1769. |
| [6] | An J Y,Kim B W.Biological desulfurization in an optical-fiber photobioreactor using an automatic sunlight collection system[J].Biotechnology,2000,80:35. |
| [7] | Henshaw P F,Zhu W.Biological conversion of hydrogen sulphide to elemental sulphur in a fixed-film continuous flow photoreactor[J].Water Res.,2001,35:3605. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%