采用Gleeble-1500热模拟实验机,对2195铝锂合金变形温度为360～520℃,应变速率为0.001～1.0 s-1的单道次热压缩及变形温度为320℃和360℃,应变速率为0.1 s-1,道次间隔时间30～180 s的双道次热压缩的流变应力及静态软化规律进行了模拟研究.通过对幂指数应力函数中系数Α和β与应变关系的分析,以及采用平均软化法考虑前一道次变形的残余应变对后一道次变形的影响,建立了2195铝锂合金多道次热变形的流变应力方程.
参考文献
| [1] | 熊焕.低温贮箱及铝锂合金的应用[J].导弹与航天运载技术,2001(06):33-40,46. |
| [2] | Castro Fernandez F R;Selllars C M;Whiteman J A .[J].Materials Science and Technology,1990,6(05):453. |
| [3] | Shi H;McLaren AJ;Sellars CM;Shahani R;Bolingbroke R .Constitutive equations for high temperature flow stress of aluminium alloys[J].Materials Science and Technology: MST: A publication of the Institute of Metals,1997(3):210-216. |
| [4] | Mcqueen H J;Ryum N .[J].Scandinavian Journal of Metallurgy,1985,14:183. |
| [5] | 沈键;李德峰 .[J].稀有金属材料与工程,1996,26(05):26. |
| [6] | Mcqueen H J .[J].Journal of Materials Processing Technology,1993,37:3. |
| [7] | Liu X;Solberg J K;Gjengedal R et al.[J].Materials Science and Technology,1995,3(11):469. |
| [8] | Furu T.;Baxter GJ.;Sellars CM.;Shercliff HR. .The influence of transient deformation conditions on recrystallization during thermomechanical processing of an Al-1% Mg alloy[J].Acta materialia,1999(8):2377-2389. |
| [9] | 张辉 .铝合金多道次热轧显微组织演变的模拟研究[D].中南工业大学,2000. |
| [10] | 韩冬峰,郑子樵,蒋呐,李劲风.高强可焊2195铝-锂合金热压缩变形的流变应力[J].中国有色金属学报,2004(12):2090-2095. |
| [11] | Chia E H;McQueen H J.Deformation[A].PA:TMS,1985:179. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%