通过冷喷涂技术在350、450和550℃条件下将机械混合的Ti/Al粉末进行沉积获得3种Ti/Al涂层,通过扫描电子显微镜、X射线衍射表征Ti/Al涂层的微观组织形貌和物相结构,采用显微硬度计测量涂层硬度值,并对涂层的耐磨粒磨损性能进行研究.结果表明,3种涂层组织致密,其中以550℃喷涂温度条件下所制备涂层孔隙率最低(0.98％),且Ti颗粒不均匀地分布在变形的Al相中;冷喷后3种涂层物相与粉末相同,仍为Ti和Al两相;3种Ti/Al涂层的硬度值分别为(81.58±17.42) HV0.3,(82.4±28.15) HV0.3和(128.4±36.98) HV0.3.3种Ti/Al涂层的磨损机制为犁沟切削形式,其中以喷涂温度为550℃所制备的涂层磨损失量最小(13.93±1.21) mg.
参考文献
| [1] | 董世运,徐滨士,王海斗.失效分析与预防、表面工程和再制造工程[J].国外金属加工,2006(01):43-47. |
| [2] | 赵文轸.金属材料表面新技术[M].西安:西安交通大学出版社,1992 |
| [3] | 王丽辉.浅谈材料的磨损失效与预防[J].黑龙江科技信息,2008(29):56. |
| [4] | 温诗铸.摩擦学原理[M].北京:清华大学出版社,1990 |
| [5] | 翟金坤.金属高温腐蚀[M].北京:北京航空航天大学出版社,1994 |
| [6] | 周永权,赵洋,王璞.表面强化技术的研究及其应用[J].机械管理开发,2010(05):104-105. |
| [7] | 孙振宇.表面强化技术在机械零件中的应用[J].煤矿机械,2008(10):85-86. |
| [8] | Wang B Q .Erosion-corrosion of coatings by biomass-fired boiler fly ash[J].WEAR,1995,188(1/2):40-48. |
| [9] | Bjordal M;Bardal E;Rogne T .Combined erosion and corrosion of thermal sprayed WC and CrC coatings[J].Surface and Coatings Technology,1995,70(2/3):215-220. |
| [10] | Wirojanupatump S .Characterization and wear performance of HVOF sprayed CrxCy-NiCr coatings[D].Nottingham:University of Nottingham,1999. |
| [11] | Berger L M;Saaro S;Naumann T et al.Microstructure and properties of HVOF-Sprayed WC-(W,Cr)2C-Ni coatings[J].Journal of Thermal Spray Technology,2008,17(3):395-403. |
| [12] | Roy M;Pauschitz A;Bernardl J et al.Microstructure and mechanical properties of HVOF sprayed nanocrystalline Cr3C2-25 (Ni20Cr) coating[J].Journal of Thermal Spray Technology,2006,15(3):372-381. |
| [13] | Horlock A J;McCartney D G;Shipway P H.Thermally sprayed Ni (Cr)-TiB2 coatings using powder produced by self-propagating high temperature synthesis: microstructure and abrasive wear behaviour[J].Material Science Engineering A,2002(1):88-98. |
| [14] | Mizuno H;Kitamura J;Tawada S.Development of durable spray coating in molten Al and Al-Zn alloys[A].Nagoya,Japan,2005:81-82. |
| [15] | Zakeri M;Rahimipour M R;Khanmohammadian A.Preparation of NiAl-TiC nanocomposite by mechanical alloying[J].Journal of Materials Science,2008(43):6912-6919. |
| [16] | Javadi M M;Edris H;Salehi M .Plasma sprayed NiAl intermetallic coating produced with mechanically alloyed powder[J].Journal of Material Science Technology,2011,27(9):816-820. |
| [17] | 李文亚,黄春杰,余敏,廖汉林.冷喷涂制备复合材料涂层研究现状[J].材料工程,2013(08):1-10. |
| [18] | 周香林;张济山;巫湘坤.先进冷喷涂技术与应用[M].北京:机械工业出版社,2011 |
| [19] | 陈枭,王洪涛,纪岗昌,白小波,董增祥,杨凤根.不同尺度碳化物粉末冷喷沉积WC-17％Co涂层的组织及性能[J].焊接学报,2013(07):38-42. |
| [20] | Novoselova T;Fox P;Morgan R;Neill W O' .Experimental study of titanium/aluminium deposits produced by cold gas dynamic spray[J].Surface and Coatings Technology,2006,200:2775-2783. |
| [21] | Zhang D;Shipway P.H;McCartney D G .工艺参数变化对冷喷铝沉积性能的影响[J].中国表面工程,2008,21(4):1-7. |
| [22] | 贾利,杨素媛.AZ31镁合金冷喷涂纳米晶铝涂层腐蚀性能[J].材料热处理学报,2014(10):195-198. |
| [23] | 陈枭,纪岗昌,王洪涛,白小波,王玉伟.超音速火焰喷涂工艺对TiB2-50Ni涂层性能的影响[J].材料热处理学报,2013(11):156-163. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%