Hexagonally well-faceted microcrystals of ZnO have been grown by thermal evaporation of Zn powder in oxygen ambient at 700℃ under atmospheric pressure. It has been observed that the properties (size and quality) of ZnO microcrystals have a strong dependence on the reactor temperature at which the oxygen gas is admitted into the growth zone. The microcrystals grown with oxygen admittance at 450℃ have a length of 1 μm and a diameter of 0.75 μm while that grown with oxygen admittance at 600 ℃ have a length of 1.5-2 μm and a diameter of 1 μm. Room temperature photoluminescence spectra show a ultraviolet (UV) emission peak at 385 nm with a green band emission at around 500 nm. The UV-to-green band emission ratio for the microcrystals grown with oxygen admittance at 450℃ is observed to be 1.25 and the ratio decreases to 0.45 for the sample grown with oxygen admittance at 600℃.
参考文献
| [1] | Q. H. Li;Q. Wan;Y. J. Chen;T. H. Wang;H. B. Jia;D. P. Yu .Stable field emission from tetrapod-like ZnO nanostructures[J].Applied physics letters,2004(4):636-638. |
| [2] | Q. Wan;Q. H. Li;Y. J. Chen;T. H. Wang;X. L. He;J. P. Li;C. L. Lin .Fabrication and ethanol sensing characteristics of ZnO nanowire gas sensors[J].Applied physics letters,2004(18):3654-3656. |
| [3] | Y.W. Heo;D.P. Norton;L.C. Tien;Y. Kwon;B.S. Kang;F. Ren;S.J. Pearton;J.R. LaRoche .ZnO nanowire growth and devices[J].Materials Science & Engineering, R. Reports: A Review Journal,2004(1/2):1-47. |
| [4] | A Umar;S Lee;Y H Im .Flower-shaped ZnO nanostructures obtained by cyclic feeding chemical vapour deposition: structural and optical properties[J].Nanotechnology,2005(10):2462-2468. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%