采用合成锆钛酸铅粉料,制备固相为49%(体积分数,下同)的浆料,以水基凝胶流延成型工艺流延出超薄料带.讨论了工艺条件对成型及样品质量的影响,加入复合塑化剂,可获得柔韧性良好的超薄料带;经冲片、烧成后可以得到超薄大规格(Φ 50 mm×0.05 mm或Φ 100mm×0.1 mm)压电陶瓷换能片;烧成样品的显微结构及压电性能与轧膜成型换能片相当.
参考文献
| [1] | Chartier T;Bruneau A .[J].Journal of the European Ceramic Society,1993,12:243. |
| [2] | Doreau F;Tari G;Pagnoux C et al.[J].Journal of the European Ceramic Society,1998,18:311. |
| [3] | Briscoe B J;Biundo G L;Ozkan N .[J].Key Engineering Materials,1997,132:345. |
| [4] | Annika Kristoffersson;Carlistr M Elis .[J].Journal of the European Ceramic Society,1997,17:289. |
| [5] | Pagnoux C;Chartier T .[J].Journal of the European Ceramic Society,1998,18:241. |
| [6] | 向军辉.[J].High Technology Letters,2002:02. |
| [7] | 马景陶;谢志鹏 et al.[J].无机材料,2002,17(03):480. |
| [8] | Ford R W.Ceramic Drying[M].Oxford:Pergamon Press,1986 |
| [9] | Descamps M;Mascart M;Thierry B et al.[J].American Ceramic Society Bulletin,1995,74(10):89. |
| [10] | 黄勇,向军辉,谢志鹏,杨金龙.陶瓷材料流延成型研究现状[J].硅酸盐通报,2001(05):22-27. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%