采用高分辨透射/扫描电镜,X射线衍射和俄歇探针等分析手段对实用型的FU-6051电子管的碳化Mo-La2O3阴弱极显微组织结构进行了观察分析.碳化Mo-La2O3阴极碳化层为疏松多孔的Mo2C块状组织,其中有许多垂直于丝轴方向的晶界与孔洞串,相互贯通直至阴极表面.碳化层与芯部基体钼结合良好,两者间无明显的过渡层.活性物质La2O3在阴极的碳化层和基体中分布均匀,但在阴极表面有相当程度的富集.La2O3在碳化层中以两种方式存在:在晶界、孔洞中以微米级的颗粒富集,在Mo2C晶体内部弥散分布纳米级La2O3粒子.
参考文献
| [1] | Baxbanm C;Cessinges G .Reaction cathode[P].US Patent 4019081,1977. |
| [2] | Baxbaum C;Gessinges G .Lanthanated thermionic cathodes[P].US Patent 4083811,1978. |
| [3] | Buxbaum C;Baden .The La-Mo cathode-A new thermionic high-performance metal cathode[J].Brown Boveri Review,1979,1:43. |
| [4] | Goebel D M;Forrester A T;Johnston S .La-Mo emitter in hollow cathode[J].Review of Scientific Instruments,1980,51(11):1468. |
| [5] | Goebel D M;Hirooka Y;Campbell G .A Large area lanthanum molybdenum electron emitters[J].Review of Scientific Instruments,1985,56(10):1888. |
| [6] | Frand B;Gartuer G .Method of manufacturing a thermionic cathode and thermionic cathode manufactured by means of said methof[P].US Patent 4533852,1985. |
| [7] | 万小峰,张久兴,周文元,李湘波,周美玲.FU105大功率广播发射管用碳化镧钼阴极研究[J].稀有金属材料与工程,2005(01):116-119. |
| [8] | Zhang Jiuxing;Zhou Wenyuan;Zhou Meiling;Zuo Tieyong.The La2O3-Doped Molybdenum Cathode for Thermionic Application[A].Russia,2002 |
| [9] | 周文元,张久兴,周美玲,王金淑,杜玮,左铁镛,李保真.La2O3-Mo阴极碳化工艺研究[J].材料科学与工艺,2002(01):66-68. |
| [10] | 聂祚仁;左铁镛;周美玲 .稀土金属热阴极中的超额镧[J].中国稀土学报,1999,17:467. |
| [11] | 王金淑,李保真,周美玲.La-Mo阴极发射性能及机理研究[J].真空电子技术,2007(06):5-7,11. |
| [12] | 郝世明,聂祚仁.钨热阴极发射机制的研究进展[J].中国钨业,2007(03):15-18. |
| [13] | 王金淑;周美玲.电子发射材料[M].北京:北京工业大学出版社,2008:123. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%