Abstract： In order to study calcium leaching behavior for the steelmaking slag, factors that influence the leaching yield have been optimized. The results show that granularity of the slag, liquid to solid ratio (in short for L/S), temperature and reaction time have a significant effect on the leaching yield. The optimal conditions for leaching are determined as follows: 1) the granularity at 75 μm, L/S at 100, temperature at 60 ℃; 2) the granularity at 75 μm, L/S at 50, temperature at 40 ℃. Finally, the optimal leaching yield under these conditions is about 15%.
参考文献
| [1] | |
| [2] | Tatsuro ARIYAMA, et al. Optimization of Ironmaking Process for Reducing CO2 Emissions in the Integrated Steel Works. ISIJ International, 2006,46(12): 1736–1744[2] Yukitaka KATO. Carbon Recycling for Reduction of Carbon Dioxide Emission from Iron-making Process. ISIJ International, 2010, 50(1):181–185[3] Cao YI, et al Experimental Research on Reducing the Dust of BOF in CO2 and O2 Mixed Blowing Steelmaking Process. ISIJ International, 2009, 49 (11): 1694–1699[4] JIN Renjie, et al. Experimental study of steelmaking with CO2 and O2 mixed blowing. Journal of University of Science and Technology Beijing, 2007, 29(supp1):78-80[5] Sebastian Teir, et al. Dissolution of Steelmaking Slags in Acetic Acid for Precipitated Calcium Carbonate Production [J]. Energy, 2007(32): 528–539[6] Sanni Eloneva, et al. Fixation of CO2 by Carbonating Calcium Derived from Blast Furnace Slag [J]. Energy, 2008(33): 1461– 1467. [7] S.N. Lekakh, et al. Investigation of a Two-Stage Aqueous Reactor Design for Carbon Dioxide Sequestration Using Steelmaking Slag [J]. Metallurgical and Materials Transactions B., 2008, 39B (3): 484-492[8] Takeshi YOSHIKAWA,et al. Preparation of Porous Ceramics by the Hydrothermal Reaction of Blast Furnace Slag for Use in a Water-retentive Material. ISIJ International, 2008, 48 (9):1322–1324[9] YE Guo-hua,et al , Pretreatment for V-bearing Steelmaking Slag by Beneficiation Methods and its Effect on Followed Leaching Procedure. The Chinese Journal of Nonferrous Metals, 2010, 20(11):2233-2238[10] Liu Yngjin, Experimental Research on Ca Leaching from Steelmaking Slag. Journal of the Chinese Rare Earth Society, 2008, 26(spec. issue):94-97 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%