为了研究上浆剂和湿热处理对复合材料微观界面性能的影响，通过单丝断裂实验测试去浆处理及湿热处理前后T300、T700SC、T800S碳纤维单丝/环氧树脂体系的界面剪切强度（ IFSS），结合扫描电镜测试手段分析了纤维表面物理特性对IFSS的影响．结果表明：去浆及湿热处理均会引起三种单丝复合材料体系IFSS降低，断点形貌由X状向鞘状发生变化，但不同的单丝复合体系 IFSS 降幅以及断点形貌变化程度不同；去浆后， T700SC/环氧树脂体系 IFSS 降幅达70．67％，T300/环氧树脂体系仅下降6．05％；湿热处理72 h后，T300/环氧树脂体系IFSS下降幅度最小；湿热作用下，去浆后的单丝/环氧树脂体系IFSS的下降更为显著．
To study the influence of desizing and hygrothermal aging on micro-interface property of composites, interfacial shear strength ( IFSS ) of carbon fiber T300, T700SC, T800S/epoxy resin monofilament composite before and after desizing and hygrothermal aging were tested by using single fiber fragmentation test( SFFT) , and the surface characterization was undertaken by SEM . The results show that IFSS of carbon fibre filament/epoxy composites decreases and birefringence pattern of breakpoints changes from X-shaped to sheath after desizing or hygrothermal aging. After desizing, IFSS of T700SC/epoxy decreases by 70.67%, while that of T300/epoxy decreases by only 6.05%. IFSS of composites with T300 also decreases the least after hygrothermal treatment. Desizing also can accelerate the damage of interface in hygrothermal environment.
参考文献
| [1] | TRIPATHI D;JONES F R .Measurement of the loading-bearing capability of the fiber/matrix interface by single-fiber fragmentation[J].Composites Science and Technology,1997,57:925-935. |
| [2] | TRIPATHIT D;LOPATTANANON N;JONES F R .A technological solution to the testing and data reduction of single fiber fragmentation tests[J].Composites Part A:Applied Science and Manufacturing,1998,29(9/10):1099-1109. |
| [3] | 王茂章;贺福.碳纤维的制造、性质及应用[M].北京:科学出版社,1984:1-2. |
| [4] | SELZER R;FRIEDRICH K .Mechanical properties and fatigue behaviour of carbon fiber reinforced polymer composites under the influence of moisture[J].Composites Part A:Applied Science and Manufacturing,1997,28(06):595-604. |
| [5] | 封彤波,肇研,罗云烽,丁东,段跃新,张佐光.不同上浆剂的国产碳纤维复合材料湿热性能研究[J].材料工程,2009(10):36-40. |
| [6] | 曹霞,温月芳,张寿春,杨永岗.耐温型炭纤维乳液上浆剂[J].新型炭材料,2006(04):337-342. |
| [7] | 武海生,孙志杰,贾晶晶,李敏,顾轶卓,张佐光.高性能有机纤维单丝复合体系界面粘结性能实验研究[J].复合材料学报,2010(04):59-63. |
| [8] | 刘洪新;顾轶卓;李敏.碳纤维/环氧树脂界面湿热性能单丝断裂法测试研究[A].长沙:中国复合材料学会,2010 |
| [9] | KELLY A;TYSON W R .Tensile properties of fiber-reinforced metals:copper/tungsten and copper/molybdenum[J].Journal of the Mechanical and Physics of Solids,1965,13(06):329-350. |
| [10] | NETRAVALI A N;HENSTENBURG R B;PHOENIX S L .Interfacial shear strength studies using the single-filament-composite test I:experiments on graphite fibers in epoxy[J].Polymer Composites,1989,10(04):226-241. |
| [11] | Pickering K.L.;Murray T.L. .Weak link scaling analysis of high-strength carbon fibre[J].Composites, Part A. Applied science and manufacturing,1999(8):1017-1021. |
| [12] | KHALILI A;KROMP K .Statistical properties of weibull estimators[J].Journal of Materials Science,1991,26(04):6741-6752. |
| [13] | The Japan Carbon Fiber Manufacturers Association .Carbon fiber[EB/OL].http://www.torayca.com/index2.html,2012-07-23. |
| [14] | KISLEV T;MAROM G;BERGLUND L et al.On the nature of the opaque cylindrical regions formed at fiber break sites in a fragmentation test[J].Advanced Composite Letters,2002,11(01):7-13. |
| [15] | 王斌,金志浩,丘哲明,刘爱华.几种高性能纤维的表面性能及其对界面粘接的影响[J].固体火箭技术,2004(03):224-228. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%