利用差示扫描量热仪(DSC)、扫描电镜(SEM)和D/max2500PC全自动X射线衍射仪研究了不同时效处理制度下TiNiCr合金相变温度的变化规律.结果表明,该合金随着时效温度增加,逆马氏体相变点As、Af上升,但当时效温度高于700℃时,相变点As、Af降低.该合金在冷却过程中经历了B2→R→B19′两阶段一级相变.通过SEM和XRD衍射研究表明,该合金经时效处理产生了Ti3Ni4析出相诱发了R相变.

参考文献

[1] 赵连城;蔡伟;郑玉峰.Shape Memory Effect and Superelasticity in Alloys(合金的形状记忆效应和超弹性)[M].北京:国防工业出版社,2002
[2] Bram M;Ahmad-Khanlou A;Heckmann A et al.[J].Materials Science and Engineering,2002,337:254.
[3] Njshida M;Wayman C M .[J].Metallurgical and Materials Transactions,1986,17A:1505.
[4] Eckelmeyer K H .[J].Scripta Metallurgica,1976,10:667.
[5] Hwang C M;Meichle M;Salamon M B et al.[J].Philosophical Magazine,1983,47(09):31.
[6] 舟久保;熙康.Shape Memory Alloys (形状记忆合金)[M].北京:机械工业出版社,1992:120.
[7] Bram M;Ahmad-Khanlou A;Heckmann A et al.[J].Materials Science and Engineering,2002,337:254.
[8] Krone L;Schüller E;Bram M et al.[J].Materials Science and Engineering,2004,338:185.
[9] Federzoni L;Guenin G I .[J].Scripta Metallurgica et Materialia,1994,31(01):25.
[10] Ishida A;gawa K O;Sato M et al.[J].Metallurgical and Materials Transactions,1997,28A:1985.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%