The cold-rolled (75% reduction ratio) Ti-IF (interstitial-free) steels of 1 mm thickness were recrystallized by annealing at 810℃ for different times. The microstructure, mechanical properties and phosphorus segregation at grain boundary were investigated by means of optical microscopy (OM), tensile testing and field emission transmission electron microscopy (FE-TEM). It was observed that recrystallization was completed after an-nealing at 810℃ for 180 s. The yield strength and tensile strength decreased as annealing time increased. The FE-TEM observation showed that after the annealing treatment, the grain boundary was broadened and the dislocations with higher density of phosphorus atoms and phosphide at grain boundaries became evident. The amount of phosphorus segregated at grain boundaries increased with annealing time.
参考文献
| [1] | Emad EL-KASHIF;Kentaro ASAKURA;Koji SHIBATA .Effect of Cooling Rate after Recrystallization on P and B Segregation along Grain Boundary in IF Steels[J].ISIJ International,2003(12):2007-2014. |
| [2] | P. Ghosh;R.K. Ray;D. Bhattacharjee .Determination of the crystal structure of FeTiP-type precipitates in a few interstitial-free high-strength steels[J].Scripta materialia,2007(3):241-244. |
| [3] | S.-H. Song;H. Zhuang;J. Wu;L.-Q. Weng;Z.-X. Yuan;T.-H. Xi .Dependence of ductile-to-brittle transition temperature on phosphorus grain boundary segregation for a 2.25Cr1Mo steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):433-438. |
| [4] | P. Ghosh;R.K. Ray;B. Bhattacharya .Precipitation and texture formation in two cold rolled and batch annealed interstitial-free high strength steels[J].Scripta materialia,2006(3):271-274. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%