综述了聚对苯酰胺的结构、性能及制备,试图由此引起对PBA纤维的关注.在其结构性能上,与PPTA进行比较,显示其优异的耐老化、耐腐蚀等性能.在聚合方面,对低温溶液聚合与直接聚合等不同方法进行分析:低温溶液聚合反应条件苛刻,但可得较高特性粘度的树脂,反应所得溶液也能直接进行纺丝;而直接聚合工艺要求简单,但所得树脂特性粘度较低且反应后溶剂回收困难.PBA在纺丝方面比PPTA纤维更简单,且有更多的选择性.
参考文献
| [1] | Yang H H.Aromatic high-strength fibers[M].USA:A WileyInterscience publication,1989:119. |
| [2] | Hearle J W S;马渝茳.高性能纤维[M].北京:中国纺织出版社,2004:27. |
| [3] | Lewin M;Preston J.High technology fibers,part C[M].New York:Marcel Dekker,Inc,1993:77. |
| [4] | 王曙中;王庆瑞;刘兆峰.高技术纤维概论[M].上海:中国纺织大学出版社,1999:329. |
| [5] | Preston J;Raleigh;Smith R W et al.Process for preparing poly-para-amino-benzoic acid[P].USP:3225011,1965. |
| [6] | Johnson TA;Del N;Del W .Preparation of p-benzamide polymers and intermediates thereof[P].USP:3699085,1972. |
| [7] | 上海合成纤维研究所.芳纶-Ⅰ型纤维研究资料[M]. |
| [8] | Tsvetkov V N .[J].European Polymer Journal,1976,12:867. |
| [9] | Arpin M;Strazielle C .[J].Polymer,1977,18:591. |
| [10] | Tashiro K;Kobayashi M;Tadokoro H .[J].Macromolecules,1977,10(02):413. |
| [11] | 陈寿羲;金永泽.[J].高分子学报,1995(02):212. |
| [12] | Alfonso G C;Bianchi E;Ciferri A et al.[J].Journal of Applied Polymer Science,Applied Polymer Symposium,1978,65:213. |
| [13] | 安智珠.高分子设计的数学模拟[M].成都:电子科技大学出版社,1989:190. |
| [14] | 邓如生;魏运方;陈布宁.聚酰胺树脂及其应用[M].北京:化学工业出版社,2002:147. |
| [15] | 范铜波.[J].高分子材料,1991(03):19. |
| [16] | 余荣华 .[J].合成纤维,1990,19(04):24. |
| [17] | 吴清基;孙瑾;沈德兴 等.[J].中国纺织大学学报,1989,15(01):21. |
| [18] | Lewin M;Preston J;陈时达;王健.高技术纤维[M].北京:纺织工业出版社,1992:322. |
| [19] | Morgan P W .[J].Macromolecules,1977,10(06):1381. |
| [20] | Kwolek S L;Morgan P W;Schaefgen J R et al.[J].Macromolecules,1977,10(06):1390. |
| [21] | Morgan P W .Process for chain terminating poly(1,4-amino benzoic acid)[P].USP:3637606,1972. |
| [22] | Kwolek S L;Del W .Optically anisotropic aromatic polyamide dopes[P].USP:3671542,1972. |
| [23] | Kwolek S L;Del W .Method of increasing the initial modulus and reducing the orientation angle of undrawn poly(parabenzamide)fibers[P].USP:3888965,1975. |
| [24] | Blades H;Del H;Del W .Dry-Jet Wet Spinning Process[P].USP:3767756,1973. |
| [25] | Russo S;Mariani A;Ignatov V N et al.[J].Macromolecules,1993,26:4984. |
| [26] | Preston J;Hofferbert W L .[J].Journal of Applied Polymer Science,Applied Polymer Symposium,1978,13:65. |
| [27] | Preston J;Hofferbert W L .[J].Journal of Applied Polymer Science,1979,24:1109. |
| [28] | Yamazaki N;Matsumoto M;Higashi F .[J].Journal of Polymer Science Part A:Polymer Chemistry,1975,13:1373. |
| [29] | Higashi F;Nakano Y;Goto M et al.[J].Journal of Polymer Science Part A:Polymer Chemistry,1980,18:1099. |
| [30] | Krigbaum W R;Kotek R;Mihara Y .[J].Journal of Polymer Science Part A:Polymer Chemistry,1985,23:1907. |
| [31] | Wu G C;Tanaka H et al.[J].Journal of Polymer,1982,14(07):571. |
| [32] | Wu G C;Tanaka H et al.[J].Journal of Polymer,1982,14(10):797. |
| [33] | Tanaka H;Wu G C et al.[J].Journal of Polymer,1982,14(08):635. |
| [34] | Memeger W .[J].Polymeric Preprints(American Chemical Society Division of Polymer Chemistry),1976,17(01):163. |
| [35] | Fitzgerald J A;Irwin R S;Memeger W .[J].Macromolecules,1991,24:3291. |
| [36] | スラフアこ一 .新規ポリアミド纖維及びその製造法[P].JP:4536852,1970. |
| [37] | スラフアこ一 .ポリアミド類の製造[P].JP:4625012,1971. |
| [38] | Panar M;Beste L F .[J].Macromolecules,1977,10(06):1401. |
| [39] | 李新贵;黄美荣.高级液晶聚合物材料工程[M].上海:华东师范大学出版社,2000:34. |
| [40] | 范铜波;姜和莲;郭丽君 等.芳族聚酰胺的溶致液晶浆液[P].CN:88105416,1988. |
| [41] | 李葰;王金华;李文燕.[J].高分子材料,1991(03):31. |
| [42] | 金兴龙;冷翠秋;余荣华 .聚对苯甲酰胺纤维的制造方法[P].CN:87101052,1987. |
| [43] | 范铜波 .[J].中国纺织大学学报,1993,19(06):116. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%