采用溶胶一凝胶法在玻璃衬底上制备了Zn1-xMgxO(x=0.1、0.2、0.3、0.4、0.5、0.6)薄膜.X射线衍射谱测试结果发现,在0.1x0.3范围内薄膜仍然保持纤锌矿结构,(002)衍射峰向大角度方向移动,超过0.3时出现氧化镁立方相.对于Zn0.7Mg0.3O薄膜,在5、5.5、6℃/min的升温速率下,升温速率越快结晶程度越好.在相同升温速率下,随着退火温度从500℃升高到560℃,样品的结晶程度变好,当退火温度达到590℃时结晶程度变差.

参考文献

[1] Pearton S J;Norton D P;Ip K et al.[J].Supperlattices and Microstructures,2003,343:2534.
[2] Yang W.;Hullavarad SS.;Nagaraj B.;Takeuchi I.;Sharma RP.;Venkatesan T.;Vispute RD.;Shen H. .Compositionally-tuned epitaxial cubic MgxZn1-xO on Si(100) for deep ultraviolet photodetectors[J].Applied Physics Letters,2003(20):3424-3426.
[3] Yang J J;Fang Q Q;Wang B M et al.[J].Acta Physica Sinica,2007,56:1116.
[4] Zhang Y T;Du G T;Liu D L et al.[J].Journal of Crystal Growth,2004,268:140.
[5] Ohtomo A.;Koida T.;Masubuchi K.;Koinuma H.;Sakurai Y. Yoshida Y.;Yasuda T.;Segawa Y.;Kawasaki M. .MgxZn1-xO as a II-VI widegap semiconductor alloy[J].Applied physics letters,1998(19):2466-2468.
[6] Liu Y M;Fang Q Q;Li Y .[J].Journal of Functional Materials,2007,10:1580.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%