通过重熔试验研究Al-5Ti-1B和Al-10Sr中间合金在A356熔体中的遗传效应.结果表明:A356合金经熔体处理后流动性较母材提高17.36%,T6处理后α-Al枝晶细化,二次枝晶间距仅为16.8 pLm,共晶硅圆整,抗拉强度达269 MPa、屈服强度203MPa、伸长率12.5%、硬度92 HBW.伴随重熔,细化变质效果逐渐衰退,熔体质量下降,以致力学性能和流动性下降.试验发现固溶后快淬可减小变质衰退带来的影响.
Hereditation of Al-5Ti-1B and Al-IOSr master alloys on modified A356 alloy was studied by remelting experiments. The results show that fluidity of the modified A356 alloy increases by 17.36% after melting treatment compared with that of as-received A356 alloy. After T6 treatment for the modified A356 alloy by addition of Al-5Ti-1B and Al-10Sr master alloys,α-Al dendrite in the alloy is refined,and the secondary dendrite arm spacing is only 16. 8μm. The eutectic silicon in the modified A356 is round and spheroidal,and its tensile strength reaches 269 MPa,yield strength reaches 203 MPa,elongation percentage is about 12. 5% and Brinell hardness is 92 HBW. As the increasing of remelting time,effect for refinement and metamorphism of the master alloy gradually declines,and the fluidity of the melt and the mechanical properties of the modified A356 alloy decreasea. Fast-quenching under liquid-N2 after solution treatment can reduce the effect of metamorphism declining.
参考文献
| [1] | Tavitas-Medrano, FJ;Gruzleski, JE;Samuel, FH;Valtierra, S;Doty, HW .Effect of Mg and Sr-modification on the mechanical properties of 319-type aluminum cast alloys subjected to artificial aging[J].Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1-2):356-364. |
| [2] | Gruzleski F .Content in unmodified and Sr-modified A356 alloys-their role in pore nucleation[J].AFS Transactions,1996,22:763-767. |
| [3] | Jun Wang;Shuxian He;Baode Sun .Grain refinement of Al-Si alloy (A356) by melt thermal treatment[J].Journal of Materials Processing Technology,2003(1):29-34. |
| [4] | Greer L;Bunn A M;Tronche A .Modeling of inoculation of metallic.melts:application to grain refinement of aluminum by Al_2Ti_2B[J].Acta Materials,2000,48:2823-2835. |
| [5] | Zhang D L;Zheng H;John H St.Effect of a short solution treatment time on microstructure and mechanical properties of modified Al-7wt% Si-0.3wt% Mg alloy[J].Journal of Light Metals,2002(02):27-36. |
| [6] | L.Y. Zhang;B.D. Zhou;Z.J. Zhan .Mechanical properties of cast A356 alloy, solidified at cooling rates enhanced by phase transition of a cooling medium[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1/2):361-365. |
| [7] | Zoqui EJ.;Shehata MT.;Paes M.;Kao V.;Es-Sadiqi E. .Morphological evolution of SSM A356 during partial remelting[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):38-53. |
| [8] | Emamy A;Razaghian A;Lashgari HR;Abbasi R .The effect of Al-5Ti-1B on the microstructure, hardness and tensile properties of Al2O3 and SiC-containing metal-matrix composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):210-217. |
| [9] | 起华荣,杨钢,史庆南.Si、Mg对铝轮毂用A356合金流动性的影响[J].轻合金加工技术,2007(02):19-22,53. |
| [10] | Guang Rana;Jingèn Zhoua .The effect of hot isostatic presaing on the microstructure and tensile properties of an unmodified A356-T6 cast aluminum alloy[J].Journal of Alloys and Compounds,2006,421:80-86. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%