以PEG-4000为模板剂,采用水热法制备了具有萤石型立方相结构的Ce0.5Zr0.5O2固溶体,考察了共沉淀pH、PEG-4000添加量、水热温度、焙烧温度对样品的物相、比表面积、孔径分布、N2吸附脱附特性等的影响.结果表明:当PEG/(Ce+Zr)(摩尔比)为0.3,共沉淀pH值约为10,120℃下水热反应12 h,烧结温度为500℃时,所得产品的比表面积为146.7 m2·g-1,平均孔径为12.50 nm.
参考文献
| [1] | 尚琪,汤大钢.控制车用汽油有害物质降低机动车排放[J].环境科学研究,2000(01):32-35. |
| [2] | 时双喜;杨义飞;李荫 .汽车尾气污染的危害及控制[J].哈尔滨建筑大学学报,1999,32(02):35. |
| [3] | 陈亚芍,董涛.汽车尾气净化催化剂技术面临的问题及发展[J].陕西师范大学学报（自然科学版）,2005(04):111-114. |
| [4] | 李凯,周卫华,王学中,周泽兴.CeO2基氧化物储氧材料研究 （Ⅰ） 制备、储氧性能研究[J].中国稀土学报,2004(01):81-84. |
| [5] | 张顺海,蒋平平,郭耘,郭杨龙,王筠松,吴东方,卢冠忠.氧化共沉淀法制备纳米级铈锆固溶体[J].中国稀土学报,2003(z2):64-66. |
| [6] | Perrichon V;Retaillcau L;Bazin P;Daturi M LavalleT J C .Metal dispersion of CeO2-ZrO2 supported platinum catalysts meanured by H2 or CO chemisorptions[J].Applied Catalysis A:General,2004,260(01):1. |
| [7] | 高典楠,刘娜,杜霞如,张纯希,袁中山,王树东.不同制备方法对铈锆复合氧化物结构及性能的影响[J].中国稀土学报,2006(z2):6-9. |
| [8] | Sadovskava E M;Ivonova Y A;Pinaeva L G;Grasso G .Kinetics of oxygen exchange over CeO2-ZrO2 fluorite-based catalysts[J].Journal of Physical Chemistry A,1997,169(04):490. |
| [9] | Kim T;Vohs J M;Gorte R J;Gorte R J .Thermodynamic investigation of the redox properties of ceria-zirconium solid solutions[J].Industrial and Engineering Chemistry Research,2006,45(16):5561. |
| [10] | Masui T;Nakano K;Ozaki T;Adachi G Y,Kang Z,Eyring L .Redox behavior of ceria-zirconium solid solution modified by the chemical filling process[J].CHEMISTRY OF MATERIALS,2001,13(05):1834. |
| [11] | Lao M F;Zheng X M .Redox behaviour and catalytic properties of Ce0.5Zr0.5O2-supported palladium catalysts[J].Applied Catalysis A:General,1999,189(02):15. |
| [12] | ThammachartM;Meeyoo V;RisksomboonT;OsuwanS .Catalytic activity of CeO2-ZrO2 mixed oxide catalysts prepared via solel technique:CO oxidation[J].Catalysis Today,2001,68(1-3):53. |
| [13] | Andrievskaya E R;Gerasimyuk G I;Komienko O A .Phase equilibria in the system HfO2-ZrO2-CeO2 at 1500 ℃[J].Powder Metallurgy and Metal ceramics,2006,45(09):448. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%