采用高能离子注入的方式,在GaN衬底中掺杂引入Cr离子制备了磁性半导体.借助于X射线衍射仪(XRD)进行了注入前后结构的对比分析,没有发现新的衍射峰,并运用高分辨率X射线衍射仪(HR-XRD)分析了Mn离子注入后衬底(0002)峰的微小变化.根据原子力显微镜的结果,发现注入后的样品表面起伏比较大,发生明显的变化.通过使用超导量子干涉仪SQUID进行变温分析,在所分析的10～300K范围内,磁化强度变化幅度较小,样品在室温条件下仍然保持铁磁性.
参考文献
| [1] | Ohno H .Making nonmagnetic semiconductors magnetic[J].Science,1998,281:951. |
| [2] | Theodoropoulou N;Hebard A F;Overberg M E et al.Magnetic and structural properties of Mn-implanted GaN Appl[J].Physics Letters,2001,78:3475. |
| [3] | Reed M L;El-Masry N A;Stadelmaier H H et al.Bedair,Room temperature ferromagnetic properties of (Ga,Mn)N,Appl[J].Physics Letters,2001,79:3473. |
| [4] | Wolos A;Palczewska M;Zajac M J .Gosk,et al,Optical and magnetic properties of Mn in bulk GaN[J].Physical Review B,2004,69:115-210. |
| [5] | Takahiko Sasaki;Saki Sonoda;Yoshiyuki Yamamoto;Ken-ichi Suga;Saburo Shimizu;Kouichi Kindo;Hidenobu Hori .Magnetic and transport characteristics on high Curie temperature ferromagnet of Mn-doped GaN[J].Journal of Applied Physics,2002(10):7911-7913. |
| [6] | Ando K.Magneto-optical studies of sp-d exchange interaction in GaN:Mn with room-temperature ferromagnetism Appl[J].Physics Letters,2003:82,100. |
| [7] | Masahiko Hashimoto;Yi-Kai Zhou;Msahito Kananmura;Hajime Asahi.High temperature .ferromangnetism in Ⅲ-Ⅴ -based DMS GaCrN grown by ECR MBE[J].Solid State Communications |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%