以锂离子电池为微反应器,电化学还原NiO制备了超细镍粉。X射线衍射结果表明所得粉末为纯相Ni,晶粒尺寸约5nm。激光粒度分布测试结果表明Ni粒度分布较窄,中位径集中在200～600nm。透射电镜照片显示颗粒粒径在80～200nm之间;放电电流密度的增加和放电温度的提高都使产物粒径有变大的趋势;在分散过程中加入不同的表面活性剂,可以提高产物Ni的分散性能。
Ultra-fine nickel powders were prepared by electrochemical reduction of NiO powder using lithium-ion battery as a micro-reactor.X-ray measurement shows that the synthesized powder consists of pure nickel phase with grain size of about 5nm.Laser particle size determination shows the nickel powder has a narrow particle size distribution with D50 in the range of 200-600nm.Transmission electron microscopy shows the nickel powder is 80-200nm.The particle size increases when increasing the discharge current density and discharge temperature.The dispersion performance of nickel can be optimized by surfactants.
参考文献
| [1] | 赵军,周伟良,徐复铭,巩丽.纳米镍/炭复合材料的制备与磁性表征[J].功能材料与器件学报,2006(02):108-112. |
| [2] | 王群,葛凯勇,毛倩谨,张晓宁,周美玲.超细镍粉在电磁防护功能材料中的应用[J].新技术新工艺,2002(02):41-43. |
| [3] | 肖荣晖.稀土储氢合金的生产及其在镍氢电池中的应用[J].有色冶炼,2000(04):6-9. |
| [4] | 江治,李疏芬,赵凤起,刘子如,阴翠梅,罗阳,李上文.纳米铝粉和镍粉对复合推进剂燃烧性能的影响[J].推进技术,2004(04):368-372. |
| [5] | 柳学全,方建锋,黄乃红,李红云.国内外羰基镍技术进展及市场展望[J].粉末冶金工业,2003(03):10-13. |
| [6] | Kim KH;Lee YB;Choi EY;Park HC;Park SS .Synthesis of nickel powders from various aqueous media through chemical reduction method[J].Materials Chemistry and Physics,2004(2/3):420-424. |
| [7] | Li YD;Wang HR;Li LQ;Qian YT;Li CW .Preparation of nickel ultrafine powder and crystalline film by chemical control reduction[J].Materials Chemistry and Physics,1999(1):88-90. |
| [8] | 齐艳妮,殷德宏,王季平,王金渠.乙二醇溶剂中纳米镍的制备研究[J].材料科学与工程学报,2005(03):416-418,421. |
| [9] | Chen DH.;Wu SH. .Synthesis of nickel nanoparticles in water-in-oil microemulsions[J].Chemistry of Materials,2000(5):1354-1360. |
| [10] | 高保娇,高建峰,周加其,葛震.超微镍粉的微乳液法制备研究[J].无机化学学报,2001(04):491-495. |
| [11] | 伍贺东,陈为亮,孟德龙,张凌义,戴永年.超细镍粉制备技术研究进展[J].湿法冶金,2007(02):57-61. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%