根据界面相分离原理,以矿物油为稀释剂,O2为添加剂,采用冻胶法制备了超高分子量聚乙烯(UHMWPE)膜以及UHMWPE/SiO2杂化微孔膜,讨论了稀释剂以及无机粒子含量对膜熔融结晶性能的影响.结果表明,矿物油作为微孔稀释剂,其加入使微孔膜中UHMWPE熔点降低,结晶度减小.当SiO2与UHMWPE质量比低于8/10时,随SiO2含量增加,UHMWPE熔点变化不显著,熔限增加,结晶温度升高,相对结晶度增大,微晶尺寸减小;当SiO2加入量足够大时,相对结晶度反而减小.随SiO2其含量增加,界面孔增多,膜孔隙率提高,水通量增大,泡点孔径先增大后减小.
参考文献
| [1] | Cohen Y;Rein D M;Vaykhansky L .[J].Composites Science and Technology,1997,57:1149-1154. |
| [2] | Turell MB.;Bellare A. .A study of the nanostructure and tensile properties of ultra-high molecular weight polyethylene[J].Biomaterials,2004(17):3389-3398. |
| [3] | Kurtz SM;Muratoglu OK;Evans M;Edidin AA .Advances in the processing, sterilization, and crosslinking of ultra-high molecular weight polyethylene for total joint arthroplasty.[J].Biomaterials,1999(18):1659-1688. |
| [4] | Smith P;Lemstra P J;Booij H C .[J].Journal of Polymer Science Part B:Polymer Physics,1981,19:877-888. |
| [5] | Tsubakihara S;Nakamura A;Yasuniwa M .[J].Polymer Journal,28:489-495. |
| [6] | Lopatin G;Yen L Y et al.[P].USP:B01D 4778601,1988-10-18. |
| [7] | Takia K;Funaoka H;Kaimai N .[P].USP:B01D 6245272,2001-6-12. |
| [8] | 赵忠华,薛平,何亚东,朱复华.用TIPS法成型超高分子量聚乙烯微孔材料的机理分析[J].高分子材料科学与工程,2003(01):24-27,31. |
| [9] | 张春芳;朱宝库;徐又一 .[J].功能材料,2007,38(zk):2731-2734. |
| [10] | 王湛.膜分离技术基础[M].北京:化学工业出版社,2000:240-283. |
| [11] | Kim J M;Min B R;Perk H C et al.[J].Journal of Applied Polymer Science,2001,81:3481-3488. |
| [12] | Benedetti E;Catanorchi S;Alessio A D et al.[J].Polymer International,1996,41:35-41. |
| [13] | 郑领英.国外膜技术在食品工业中的应用现状和发展动向[J].水处理技术,1994(05):247. |
| [14] | Smook J;Pennings J .[J].Colloid and Polymer Science,1984,262:712-722. |
| [15] | Xiao Changfa;Zhang Yufeng;An Shulin et al.[J].Journal of Applied Polymer Science,2000,77:2877-2881. |
| [16] | 赵华山;姜胶东;吴大城.高分子物理[M].北京:纺织工业出版社,1982:209-210. |
| [17] | 何曼君;陈维孝;董西侠.高分子物理[M].上海:复旦大学出版社,1988:70-73. |
| [18] | Wunderlich B.Macromolecular Physics[M].New York:Academic Press,Inc,1976 |
| [19] | 铉晓群 .超高分子量聚乙烯的溶解及中空纤维纺制工艺的研究[D].东华大学,2006. |
| [20] | Wang KH.;Choi MH.;Koo CM.;Xu MZ.;Chung IJ.;Jang MC.;Choi SW.;Song HH. .Morphology and physical properties of polyethylene/silicate nanocomposite prepared by melt intercalation[J].Journal of Polymer Science, Part B. Polymer Physics,2002(14):1454-1463. |
| [21] | 马传国,容敏智,章明秋.纳米碳酸钙及其表面处理对等规聚丙烯结晶行为的影响[J].高分子学报,2003(03):381-386. |
| [22] | 杨华明,曹建红,敖伟琴,邱冠周.无机粒子/聚合物复合材料的结晶行为[J].高分子材料科学与工程,2003(03):68-71. |
| [23] | 马继盛,漆宗能,李革,胡友良.聚丙烯/蒙脱土纳米复合材料的等温结晶研究[J].高分子学报,2001(05):589-593. |
| [24] | Laxminarayan A;Meguire K S;Kim S S .[J].Polymer,1994,35(14):3060-3068. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%