制备稳定的全氟烷基丙烯酸酯改性阳离子聚氨酯复合乳液,并通过红外和核磁共振氟谱对其结构进行表征。将其应用在纸张表面处理上,重点研究阳离子扩链剂N-甲基二乙醇胺（MDEA）用量及功能性单体全氟烷基丙烯酸酯（FA）用量对纸张表面防水防油性能和力学性能的影响。接触角分析表明随MDEA用量增大,纸张防水性和防油性先增大后减小;随FA用量增大,防水性和防油性均增大。经m（FA）=30%的FAPU复合乳液处理过的纸张,水和油在其上所成初始接触角分别可达132和114°,并且在300s测试时间内,其随时间变化很小。力学性能测定表明MDEA和FA用量增大,纸张抗张强度增大。纸张表面和断面扫描电镜观察表明,经FAPU处理过的纸样其纤维结合更加紧密。
The perfluorinated acrylate modified cationic polyurethane（FAPU） hybrid emulsion was prepared and characterized by IR and F19 NMR.The FAPU hybrid emulsion was used for paper surface sizing.The emphasis was put on the influence of the content of MDEA as cationic extender and the content of FA as functional monomer on the paper properties.The contact angles result shows that the water and oil-repellency property of the papers treated with FAPU increased and then decreased with the MDEA content increase,while the water and oil-repellency property both increased with the increase of FA content.The initial contact angles of water and liquid paraffin on the paper treated with FAPU of 30% content FA were 132 and 114°,respectively.In addition,the contact angles changed little within 300s which indicated that the paper treated with FAPU possessed good water and oil-repellency ability.The mechanical property test results show the paper tensile strength increased with the increase of the MDEA and FA contents.At last,the surface and crosssection of the paper untreated and treated with FAPU were observed by SEM,respectively.The result shows that the fibers of the treated paper more closely combined.
参考文献
| [1] | Liu Shuguang;Zhu Guoquan .[J].European PolymerJournal,2007,43(09):3904-3911. |
| [2] | Min Jiang;Zhaohui Zheng;Xiaobin Ding .Convenient synthesis of novel fluorinated polyurethane hybrid latexes and core-shell structures via emulsion polymerization process with self-emulsification of polyurethane[J].Colloid and polymer science,2007(9):1049-1054. |
| [3] | Chai Shuling;Jin Martinming;Tan Huimin .[J].European Polymer Journal,2008,44(10):3306-3313. |
| [4] | Jiang Min;Zhao Xiuli;Ding Xiaobin et al.[J].European Polymer Journal,2005,41(08):1798-1803. |
| [5] | Shi Yuanchang;Wu Youshi;Zhu Zhiqian .[J].Journal of Applied Polymer Science,2003,88(02):470-475. |
| [6] | 赵艳娜,沈一丁.交联改性苯乙烯-丙烯酸酯树脂纸张表面施胶增强剂的制备及应用[J].功能材料,2011(03):533-536. |
| [7] | Byounggak K;Eunho S;Kilwon C et al.[J].European Polymer Journal,2008,44(09):2912-2919. |
| [8] | Chen Yanjun;Zhang Chaocan;Chen Xinxin .[J].European Polymer Journal,2006,42(03):694-701. |
| [9] | Xiao Xinyan;Wang Ye .[J].Colloids and Surfaces A:Physicochemical and Engineering Aspects,2009,348(1-3):151-156. |
| [10] | 李刚辉,李小瑞,沈一丁.聚氨酯-含氟丙烯酸酯复合乳液的制备及其表面性能[J].化工学报,2006(01):192-196. |
| [11] | Zhang Chuyin;Zhang Xingyuan;Dai Jiabing et al.[J].Progress in Organic Coatings,2008,63(02):238-244. |
| [12] | Xin Hua;Shen Yiding;Li Xiaorui .[J].Colloids and Surfaces A:Physicochemical and Engineering Aspects,2011,384(1-3):205-211. |
| [13] | 汪江节,陈建兵,王武生,曾俊.含氟丙烯酸酯改性水性聚氨酯涂饰剂的制备[J].皮革化工,2006(05):37-39. |
| [14] | 钟倪,袁荞龙.阳离子水性聚氨酯的合成与性能[J].过程工程学报,2008(02):366-371. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%