采用微波水热法制备 (Ni0.30Cu0.20Zn0.50)Fe2O4·xMg(x=0、0.01、0.02、0.03、0.04)粉末,并用该纳米粉在900℃/4h下,烧结形成了致密的陶瓷体.对低温烧结掺Mg的Ni-Cu-Zn铁氧体的成相,致密化过程及Mg含量对样品显微结构和电磁性能的影响进行了研究.研究结果表明,在Mg含量为0.01～0.04范围内,掺Mg可以影响样品的晶胞参数,增加样品的烧结密度并且改善样品的微观结构和电磁性能.其中Mg含量为0.04时,样品的晶粒尺寸大而均匀,初始磁导率、电阻率、Q值比其它掺量的高.
参考文献
| [1] | Chen WP;Wang J;Wang DY;Wang Y;Qi JQ;Chan HLW .Hydrogen-induced resistance degradation in NiCuZn ferrites[J].Physica, B. Condensed Matter,2004(1/2):41-45. |
| [2] | Yue Zhenxing;Zhou Ji;Gui Zhilun .[J].Journal of Magnetism and Magnetic Materials,2003,264(2-3):258-263. |
| [3] | 韩志全.叠层片式电感及低温烧结铁氧体的研发进展[J].磁性材料及器件,2004(06):6-10. |
| [4] | Kagotani T;Kobayashi R;Sugimoto S .[J].Journal of Magnetism and Magnetic Materials,2005,290-291(02):1442-1445. |
| [5] | Kim C W;Koh J G .[J].Journal of Magnetism and Magnetic Materials,2003,257(2-3):355-368. |
| [6] | Krishnaveni T;Rajini Kanth B;Rama V S .[J].Journal of Alloys and Compounds,2006,414(1-2):282-286. |
| [7] | Allegri P;Autissier D;Taffary T .[J].Journal of Key Engineering Material,1997,132-136(02):1424-1427. |
| [8] | Roy P K;Bera J .[J].Journal of Magnetism and Magnetic Materials,2006,298:38-42. |
| [9] | 田民波.磁性材料[M].北京:清华大学出版社,2001 |
| [10] | 张有纲;黄永杰;罗迪民.磁性材料[M].成都:成都电讯工程学院出版社,1988 |
| [11] | 周济;吴海燕;桂治轮 等.[J].功能材料,1997,28(01):22-25. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%