用X射线衍射(XRD)、激光拉曼光谱(LRS)、程序升温还原(TPR)、催化剂晶格氧反应性和微反测试等手段考察了BiCeVMoO复合氧化物催化剂的组成、结构、氧化-还原性质与催化丙烷选择氧化性能. 结果表明,n(Ce)/n(Ce+Bi)≤0.15时,Ce组分可能占据BiVMoO结构中Bi离子所处的晶格位置. 催化剂对丙烷选择氧化的催化性能与Ce组分的含量密切相关,随着Ce含量的增加,丙烯醛选择性显著升高,在n(Ce)/n(Ce+Bi)=0.15时达极大值. 随着Ce含量的进一步增加,丙烯醛选择性下降,完全氧化产物COx选择性上升. 可以认为,适量Ce组分的引入提高了催化剂晶格氧物种的反应活性,从而改善了催化剂对丙烷选择氧化的催化性能.
参考文献
| [1] | Brazdil J F;Gleaser L C;Grasselli R K .[J].Journal of Catalysis,1983,81(01):142. |
| [2] | Burrington J D;Kartisek C T;Grasselli R K .[J].Journal of Catalysis,1984,87(02):363. |
| [3] | Moro-Oka Y;Ueda W .[J].Advances in Catalysis,1994,40:233. |
| [4] | Kim Y-C;Ueda W;Moro-oka Y .[J].Applied Catalysis,1991,70(01):175. |
| [5] | Kim Y-C;Ueda W;Moro-oka Y .[J].Catalysis Today,1992,13(04):673. |
| [6] | Baerns M;Buyevskaya O V;Kubik M;Maiti G,Ovsitser O,Seel O .[J].Catalysis Today,1997,33(01):85. |
| [7] | Bettahar M M;Costentin G;Savary L;Lavally J C .[J].Applied Catalysis A:General,1996,145:1. |
| [8] | Sleight A W.[M].New York:Academic Press,1977:181. |
| [9] | 杨汉培,范以宁,冯令云,邱金恒,林明,许波连,陈懿.铋钒钼复合氧化物催化剂结构与丙烷选择氧化催化性能[J].化学学报,2002(06):1006-1010. |
| [10] | 杨汉培,范以宁,林明,许波连,陈懿.铋钼复合氧化物催化剂的结构及其对丙烷选择氧化反应的催化性能[J].催化学报,2001(06):515-519. |
| [11] | Villa P L;Szabo A;Trifiro F .[J].Journal of Catalysis,1977,47(01):122. |
| [12] | Hardcastle F D;Wachs I E .[J].Journal of Physical Chemistry,1991,95(13):5031. |
| [13] | Krasovec U O;Orel B;Surca A;Bukovec N,Reisfeld R S .[J].Solid State Ionics,1999,118(3-4):195. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%