The characteristics of dynamic reerystallization (DRX) in Mg-Y-Nd-Gd-Zr-RE magnesium alloy were investigated by compres-sion tests at temperatures between 523 and 723 K and at strain rates ranging from 0.002 to 1 s-1 with maximum strain of 0.693. The strain-hardening rate can be obtained from true stress-true strain curves, plots of θ-σ,-(θ/ σ)-σ and lnθ-σ in different compression conditions were obtained by further study. The critical condition of the onset of DRX process was determined as ((/ σ)(-θ/ σ))=0. In the range of the above deformation temperature and strain rate, the ratio of critical stress (σc) to peak stress (am) and critical strain (εc) to the peak strain (εm) stood at σc/σm=0.62-0.89 and εc/εm=0.11-0.37, respectively. DRX could be observed during hot deformation process, microstructure evolution of the magnesium alloy at different temperatures and strain rates were studied with the aid of optical microscope(OM), and the average recrystal-lized grain size was measured by means of intercepts on photomicrographs. It was shown that the average dynamically recrystallized grain size (drec) changed with different deformation parameters, the natural logarithm of the average recrystallized grain size varied linearly with the natural logarithm of Zener-Hollomon parameter; the peak stress changed with the average recrystallized grain size, and the natural loga-rithm of the average recrystallized grain size varied linearly with the natural logarithm of the peak stress.
参考文献
| [1] | Mordike B L .Magnesium and magnesium alloys[J].Light Metals,2001,51(02) |
| [2] | McQueen H J;Evangelism E;Bowles J;Crawford G .Hot deformation and dynamic recrystallization of Al-5Mg-0.8Mn alloy[J].Metal Science Journal,1984,18(08):395. |
| [3] | Ion S E;Hunphreys F J;White S H .Ynamic recrystallization and the development of microstructure during the high temperature deformation of magnesium[J].ACTA MATERIALIA,1982,30:1909. |
| [4] | Zhang Ya;Zeng Xiaoqin;Lu Chen;Ding Wenjiang .Deformation behavior and dynamic recrystallization of a Mg-Zn-Y-Zr alloy[J].Materials Science and Engineering,2006,A428:91. |
| [5] | Galiyev A;Kaibyshev R;Gottstein G .Correlation of plastic deformation and dynamic recrystallization in magnesium alloy ZK60[J].Acta Materialia,2001,49:1199. |
| [6] | Poliak E I;Jonas J J .A one-parameter approach to determining the critical conditions for the initiation of dynamic recrystallization[J].Acta Materialia,1996,44:127. |
| [7] | LI Shu-bo;WANG Yan-qiu;ZHENG Ming-yi .Dynamic recrystallization of AZ91 magnesium alloy during compression deformation at elevated temperature[J].Transactions of Nonferrous Metals Society of China,2004(2):306-310. |
| [8] | 汪凌云,黄光胜,范永革,黄光杰.变形AZ31镁合金的晶粒细化[J].中国有色金属学报,2003(03):594-598. |
| [9] | 郭强,严红革,陈振华,张辉.AZ31镁合金高温热压缩变形特性[J].中国有色金属学报,2005(06):900-906. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%