在NENE-2型微动疲劳试验机上对弯-弯条件下PD3、U71Mn钢的疲劳裂纹扩展特性进行了研究.结果表明:相同弯-弯条件下,U71Mn钢中的疲劳裂纹较PD3钢中的短,因而具有较好的抗疲劳性能;其原因在于U71Mn钢的塑性较PD3钢的好,使得裂纹尖端钝化,同时其细小的珠光体具有更多的晶界,从而为能量的耗散提供了更多的途径,最终使得裂纹在U71Mn钢中较在PD3钢中不容易扩展.
参考文献
| [1] | 金学松,沈志云.轮轨滚动接触疲劳问题研究的最新进展[J].铁道学报,2001(02):92. |
| [2] | 孟波,郭万林.表面微观形貌对疲劳强度影响的定量分析[J].机械工程材料,2006(05):26-29. |
| [3] | Anders Ekberg;Elena Kabo .Fatigue of railway wheels and rails under rolling contact and thermal loading - an overview[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2005(7/8):1288-1300. |
| [4] | D. W. Barke;W. K. Chiu .A review of the effects of out-of-round wheels on track and vehicle components[J].Proceedings of the Institution of Mechanical Engineers. Part F, Journal of rail and rapid transit,2005(f3):151-175. |
| [5] | Jonas W. Ringsberg .Life prediction of rolling contact fatigue crack initiation[J].International Journal of Fatigue,2001(7):575-586. |
| [6] | A. Bernasconi;P. Davoli;M. Filippini;S. Foletti .An integrated approach to rolling contact sub-surface fatigue assessment of railway wheels[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2005(7/8):973-980. |
| [7] | 刘启跃,张波,周仲荣.铁路钢轨损伤机理研究[J].中国机械工程,2002(18):1596-1599. |
| [8] | 钟雯,赵雪芹,王文健,刘启跃.PD3与U71Mn钢轨疲劳裂纹扩展特性研究[J].中国机械工程,2008(14):1740-1743. |
| [9] | 赵雪芹 .钢轨接触疲劳裂纹形成机理研究[D].西南交通大学,2006. |
| [10] | 孙春方,王成龙.TLVW1114Ti钢疲劳特性研究[J].机械工程材料,2003(02):52-54. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%