采用扫描电子显微镜(SEM)对多熔体多次注射成型(MMMIM)聚苯乙烯(PS)/聚乙烯(PE)共混物制品的相形态结构进行了研究,发现MMMIM制品呈现出特殊的“双皮-芯”结构,且不论是在MMMIM制品的皮层材料区域还是在芯层材料区域,分散相PS的形态结构在制品的近浇口端和远浇口端均存在着显著差异,即在近浇口端处有大量取向的纤维状结构形成,而在远浇口端只有少量椭球状或棒状结构形成.在形态分析的基础上,结合MMMIM成型原理,探讨了熔体穿透作用对多熔体多次注射成型制品形态的形成及分布的影响.

参考文献

[1] 张凯,刘正英,孙囡,汪龙,杨斌,陆颖,杨鸣波.多流体多次注射成型HDPE制品的结晶形态[J].高分子学报,2011(03):235-239.
[2] SELDEN R. .Co-injection Molding: Effect of Processing on Material Distribution and Mechanical Properties of a Sandwich Molded Plate[J].Polymer engineering and science,2000(5):1165-1176.
[3] Schlatter G;Davidoff A;Vincent M;Agassant JF .An unsteady multifluid flow model: application to sandwich injection molding process[J].Polymer engineering and science,1999(1):78-88.
[4] Zhang, K.;Liu, Z.;Yang, B.;Yang, W.;Lu, Y.;Wang, L.;Sun, N.;Yang, M. .Cylindritic structures of high-density polyethylene molded by multi-melt multi-injection molding[J].Polymer: The International Journal for the Science and Technology of Polymers,2011(17):3871-3878.
[5] 郑国强,杨伟,杨鸣波,黄鹂,李尉,刘春太,申长雨.气体辅助注射成型PC/PE共混物的形态[J].高分子材料科学与工程,2006(05):193-196.
[6] Zheng GQ;Yang W;Yin B;Yang MB;Liu CT;Shen CY .Morphology of gas-assisted and conventional injection molded polycarbonate/polyethylene blend[J].Journal of Applied Polymer Science,2006(3):3069-3077.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%