以聚醚多元醇、2,4-甲苯二异氰酸酯和甲基丙烯酸羟乙酯为原料合成端基含双键的聚氨酯封端预聚体,再加入苯乙烯单体和2-羟基-2-甲基-1-苯基-1-丙酮光敏引发剂,在紫外光照下以自由基共聚合方式合成聚氨酯/苯乙烯弹性体复合材料.研究了苯乙烯单体用量、光照时间和引发剂用量对复合材料性能的影响,并用红外光谱(FT-IR)和差示扫描量热分析(DSC)对产物进行了表征.结果表明,聚氨酯封端预聚体与苯乙烯单体质量比为10∶9,引发剂质量为苯乙烯单体的0.6％,紫外光固化3h时,产物力学性能良好,且为无规共聚结构.
参考文献
| [1] | 章鹏,张兴元,戴家兵.二聚酸聚酯二醇基可紫外光固化水性聚氨酯的合成与性能[J].高分子材料科学与工程,2011(10):23-26. |
| [2] | Chenyan Bai;Xingyuan Zhang;Jiabing Dai .Synthesis of UV crosslinkable waterborne siloxane-polyurethane dispersion PDMS-PEDA-PU and the properties of the films[J].JCT research,2008(2):251-257. |
| [3] | Jung, D.H.;Kim, E.Y.;Kang, Y.S.;Kim, B.K. .High solid and high performance UV cured waterborne polyurethanes[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2010(1/3):58-63. |
| [4] | Hwang, H.-D.;Park, C.-H.;Moon, J.-I.;Kim, H.-J.;Masubuchi, T. .UV-curing behavior and physical properties of waterborne UV-curable polycarbonate-based polyurethane dispersion[J].Progress in Organic Coatings: An International Review Journal,2011(4):663-675. |
| [5] | C. Decker;F. Masson;R. Schwalm .Weathering resistance of waterbased UV-cured polyurethane-acrylate coatings[J].Polymer Degradation and Stability,2004(2):309-320. |
| [6] | Rodriguez R;Alarcon CD;Ekanayake P;McDonald PJ;Keddie JL;Barandiaran MJ;Asua JM .Correlation of Silicone Incorporation into Hybrid Acrylic Coatings with the Resulting Hydrophobic and Thermal Properties[J].Macromolecules,2008(22):8537-8546. |
| [7] | 吴校彬,傅和青,黄洪,陈焕钦.聚氨酯-丙烯酸酯-苯乙烯复合水分散液的粒径及形态[J].高分子材料科学与工程,2008(02):87-90. |
| [8] | 黄萍,叶代勇.分子结构中碳碳双键对水性UV聚氨酯分散体的影响[J].涂料工业,2011(10):48-53. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%