用穆斯堡尔谱研究了ZG0Cr13Mn10N钢气蚀(CE)前后的表面组织变化.结果表明,ZG0Cr13Mn10N钢气蚀前主要由亚稳定的合金奥氏体及内磁场值分别为23395.8 kA/m和21088.0 kA/m的两类合金马氏体组成;气蚀诱发γ/α转变的同时还明显改变材料表层组织中合金元素的相内分布形式,并诱发出一种合金度更高的合金马氏体(其内磁场值为18462.0 kA/m).
参考文献
| [1] | ЪогаевИНКавитационноеРазрушениеиКавитационностойкиеСплавы[M].М:Москва,1972:110. |
| [2] | ФилипповМА;ЛитвиновВС;НемировскийЮР.СталисМетастабильнымАустенитом[M].М:Москва,1988:186. |
| [3] | Zylla I M;Hougardy H P .Cavitation Behaviour of a Metastable Cr-Mn-austenite[J].Steel Research International,1994,65(04):132-137. |
| [4] | 张恒华;苏世漳;马如璋 等.Mssbauer效应在高速钢中残留奥氏体测定上的应用[J].材料科学进展,1989,3(06):536-539. |
| [5] | Vincze I .Mssbauer Measurements in Iron Based Alloys with Transition Metals[J].Journal of Physics F:Metal Physics,1973,3(03):647-663. |
| [6] | 张福成;郑炀曾 .铬锰奥氏体钢中合金元素及碳的短程有序分布[J].科学通报,1991,27(05):382-385. |
| [7] | Cook D C .Strain Induced Martensite Formation in Stainless Steel[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1987,18(02):201. |
| [8] | 张慧友;陈鉴寅;蒋劲 .利用穆斯堡尔谱效应对GCr15轴承钢作物相分析[J].理化检验-物理分册,1989,25(03):25. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%