采用离子束辅助磁控溅射技术(IBAMS)沉积Cr-N硬质镀层,用压入法评定镀层的断裂韧性,多次冲击试验法测定镀层的多冲疲劳抗力,探讨了多冲疲劳抗力与镀层组织结构和断裂韧性等机械性能的关系.结果表明,通过调节离子束辅助轰击能量,可以提高Cr-N镀层的硬度和断裂韧性.镀层断裂韧性的提高除了与晶块尺寸减小有关外,还与离子轰击导致镀层致密度增加相关.在冲击载荷作用下Cr-N镀层的失效方式为内聚力型疲劳剥落,随硬度和断裂韧性增加,镀层的抗多次冲击疲劳能力提高.
参考文献
| [1] | Veprek Stan .[J].Journal of Vacuum Science and Technology A,1999,A17(05):2401. |
| [2] | 吴大维.[J].Vacuum(真空),2003(06):1. |
| [3] | Kamiya S;Kimura H;Saka M et al.[J].Thin Solid Films,2001,389:180. |
| [4] | Wiklund U;Bromark M;Larsson M et al.[J].Surface and Coatings Technology,1997,91:57. |
| [5] | Lawn B R;Evans A G;Marshall D B .[J].Journal of the American Ceramic Society,1980,63:574. |
| [6] | 刘伯威,樊毅,张金生,潘进.MoSi2复合材料断裂韧性的测量及评价[J].中国有色金属学报,2001(05):810-814. |
| [7] | Mehrotra P K;Quinto D T .[J].Journal of Vacuum Science and Technology A,1985,A3(06):2401. |
| [8] | 文胜平;米彦郁;余历军.[J].PTCA (Part A:Physical Testing) (理化检验-物理分册),2004(05):225. |
| [9] | Bouzakis KD;Siganos A .Fracture initiation mechanisms of thin hard coatings during the impact test[J].Surface & Coatings Technology,2004(2/3):150-159. |
| [10] | Bouzakis K D;Siganos A;Leyendecker T et al.[J].Thin Solid Films,2004,460:180. |
| [11] | 黄鹤,王学刚,朱晓东,陈华,何家文.离子束辅助磁控溅射沉积TiN薄膜的研究[J].稀有金属材料与工程,2002(03):205-208. |
| [12] | 田林海,陈坚,唐宾,何家文,陈华.IBAD界面反应及其对结合强度的影响[J].稀有金属材料与工程,2005(01):77-81. |
| [13] | 范雄.Metal X-ray Diffraction(金属X射线学)[M].北京:机械工业出版社,1989 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%