以MgCl2·6HL2O和NH4HCO4为主要原料,在添加剂空白的条件下,采用液相微波法制备MgCO3·3HO晶须晶体,并分析了反应时间、微波辐照能量对晶体制备的影响.利用XRD、TEM等技术对制备产物进行表征.结果表明,MgCl2·6H2O和NH4HCO4混合物在微波辅助条件下反应6min,微波辐照能量400W时,合成的晶须结晶发育完整,晶须平均长度172 μm,长径比达16.86.在此基础上,进一步探讨了微波效应与三水碳酸镁晶须晶体的生长机理.
参考文献
| [1] | 闫平科,田海山,高玉娟,王斌,马正先,梁帅.高长径比三水碳酸镁晶须的合成研究[J].人工晶体学报,2012(01):158-164. |
| [2] | Freitag F;Kleinebudde P .How do roll compaction/dry granulation affect the tableting behaviour of inorganic materials? Comparison of four magnesium carbonates.[J].European journal of pharmaceutical sciences,2003(4):281-289. |
| [3] | Mitsuhashi K;Tagami N;Tanabe K;Ohkubo T;Sakai H;Koishi M;Abe M .Synthesis of microtubes with a surface of "house of cards" structure via needlelike particles and control of their pore size[J].Langmuir: The ACS Journal of Surfaces and Colloids,2005(8):3659-3663. |
| [4] | 王万平,张懿.碳酸盐热解法制备氧化镁晶须[J].硅酸盐学报,2002(z1):93-95. |
| [5] | X. Wang;D. Xue .Direct observation of the shape evolution of MgO whiskers in a solution system[J].Materials Letters,2006(25/26):3160-3164. |
| [6] | 郑亚君,党利琴,张智平,雷志斌,陈吉平.搅拌时间对水合碳酸镁形貌和组成的影响[J].精细化工,2007(09):835-838,869. |
| [7] | Wang Y;Li ZB;Demopoulos GP .Controlled precipitation of nesquehonite (MgCO3 center dot 3H(2)O) by the reaction of MgCl2 with (NH4)(2)CO3[J].Journal of Crystal Growth,2008(6):1220-1227. |
| [8] | 邵明浩,史永刚,胡泽善.碳酸镁晶须的制备、表征与分析方法[J].后勤工程学院学报,2008(01):37-40. |
| [9] | 邵平平,李志宝,密建国.碳酸镁水合物在283-363 K范围内的晶体组成及晶型[J].过程工程学报,2009(03):520-525. |
| [10] | 陈敏,李月圆,王健东,陈庆武,崔虹旭,申莹莹.利用菱镁矿制备碳酸镁晶须[J].硅酸盐学报,2009(10):1649-1653. |
| [11] | 王晓丽,薛冬峰.不同镁盐对氧化镁晶须形貌的影响[J].无机盐工业,2006(02):16-18. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%