New preparation of Mg-Li-A1 alloys by electrolysis in molten salt

金属学报(英文版), 2010, 23(2): 129-136.

^1, , ^2, , ^3, , ^4, , ^5,

1.Key Laboratory of Superlight Materials and Surface Technology,Ministry of Education,College of Material Science and chemical Engineering,Harbin Engineering University,Harbin 150001,China

2.Key Laboratory of Superlight Materials and Surface Technology,Ministry of Education,College of Material Science and chemical Engineering,Harbin Engineering University,Harbin 150001,China

3.Key Laboratory of Superlight Materials and Surface Technology,Ministry of Education,College of Material Science and chemical Engineering,Harbin Engineering University,Harbin 150001,China

4.Key Laboratory of Superlight Materials and Surface Technology,Ministry of Education,College of Material Science and chemical Engineering,Harbin Engineering University,Harbin 150001,China

5.Key Laboratory of Superlight Materials and Surface Technology,Ministry of Education,College of Material Science and chemical Engineering,Harbin Engineering University,Harbin 150001,China

基金项目: National High Technical Research and Development Programme of China(2006AA03Z510) the Scientific Technology Bureau of Harbin(2009RFLXG012) the National Natural Science Foundation of China(50871033) the Key Laboratory of Superlight Materials & Surface Technology,Ministry of Education

New preparation of Mg-Li-A1 alloys by electrolysis in molten salt

Wei HAN ^1, , Qiong CHEN ^2, , Ke YE ^3, , Yongde YAN ^4, , Milin ZHANG ^5,

1.Key Laboratory of Superlight Materials and Surface Technology,Ministry of Education,College of Material Science and chemical Engineering,Harbin Engineering University,Harbin 150001,China

2.Key Laboratory of Superlight Materials and Surface Technology,Ministry of Education,College of Material Science and chemical Engineering,Harbin Engineering University,Harbin 150001,China

3.Key Laboratory of Superlight Materials and Surface Technology,Ministry of Education,College of Material Science and chemical Engineering,Harbin Engineering University,Harbin 150001,China

4.Key Laboratory of Superlight Materials and Surface Technology,Ministry of Education,College of Material Science and chemical Engineering,Harbin Engineering University,Harbin 150001,China

5.Key Laboratory of Superlight Materials and Surface Technology,Ministry of Education,College of Material Science and chemical Engineering,Harbin Engineering University,Harbin 150001,China

Keywords： Mg-Li-Al

This work presents a study on electrochemical formation of Mg-Li-Al alloys on an inert electrode (Mo electrode) in a molten KCl-LiCl-AlCla-MgCl2-KF system. It aims at preparation Mg-Li-Al metal alloy directly under an optimal electrolytic parameters. Main factors which affect current efficiency are investigated. We have discussed the co-electrodeposition conditions and the effect of technical parameters on these experiments, and gained a good electrolytic process. The result of calculation shows that co-electrodeposition Mg, Li and Al occurs at the cathode current density higher than 9 A/cm2 and electrolytic voltage between 6 to 9 V. And at the optimal parameters, 12-13 A/cm2, 620-640 ℃, the highest current efficiency reaches as high as 86%.Lithium combined with magnesium forms Li0.92Mg4.0s and Li3Mg7, and aluminum mainly exists in a form of Mg0.58Al0.42, distributing in the alpha phases and beta phases.

参考文献

[1]	G. Liang .Synthesis and hydrogen storage properties of Mg-based alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2004(1/2):123-128.
[2]	S.J. Wang;G.Q. Wu;R.H. Li .Microstructures and mechanical properties of 5 wt. percent Al_2Y_p/Mg-Li composite[J].Materials Letters,2006(15):1863-1865.
[3]	Z. Trojanova;Z. Drozd;P. Lukac .Deformation behaviour of Mg-Li alloys at elevated temperatures[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(0):148-151.
[4]	N. Saito;M. Mabuchi;M. Nakanishi;K. Kubota;K. Higashi .The aging behavior and the mechanical properties of the Mg-Li-Al-Cu alloy[J].Scripta materialia,1997(5):551-555.
[5]	T. Liu;S.D. Wu;S.X. Li;P.J. Li .Microstructure evolution of Mg–14% Li–1% Al alloy during the process of equal channel angular pressing[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(0):499-503.
[6]	Y. W. Kim;D. H. Kim;H. I. Lee;C. P. Hong .Widmanstatten type solidification in squeeze casting of Mg-Li-Al alloys[J].Scripta materialia,1998(6):923-929.
[7]	M.C. Lin;C.Y. Tsai;J.Y. Uan .Converting hcp Mg-Al-Zn alloy into bee Mg-Li-Al-Zn alloy by electrolytic deposition and diffusion of reduced lithium atoms in a molten salt electrolyte LiCl-KCl[J].Scripta materialia,2007(7):597-600.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

New preparation of Mg-Li-A1 alloys by electrolysis in molten salt

参考文献