采用模压法制备Kevlar/Surlyn复合材料,通过研究模压温度、压力、时间等工艺参数对复合材料性能的影响,确定了最佳制备工艺,模压温度170℃,模压压力3MPa,模压时间30min。研究了树脂含量对复合材料防刺性能的影响规律,结果表明Surlyn树脂含量对复合材料的防刺性能影响显著。树脂含量为47%（质量分数）时,复合材料防刺效果最优。
Kevlar/Surlyn composites were fabricated by mould pressing. The effects of pressing temperature, pressure, time and resin content on properties of composites were studied. The results show that the optimum proceeding condition is pressing temperature 170℃ ,pressure 3MPa,holding time 30min. Resin content has im- portant effect on stab resistant property of composite. The optimum resin content was 47wt%.
参考文献
| [1] | 顾肇文.柔性复合防刺服机理研究[J].纺织学报,2006(08):80-84. |
| [2] | Liu Wei;Yang Jinlong;Xiao Meng et al.Stab-resist- ance of shear thickening fluid enhanced nylon abrics[J].Journal of Functional Materials,2011,42($4):632-634. |
| [3] | 郭静荷,姜亚明.防刺个体装甲材料的发展与现状[J].产业用纺织品,2004(06):5-8,13. |
| [4] | 韩辉,李楠.防弹纤维复合材料及其在武器装备中的应用[J].高科技纤维与应用,2005(01):40-43. |
| [5] | 周祥兴;任显诚.塑料包装材料成型及应用技术[M].北京:化学工业出版社,2004 |
| [6] | Jessie B;Mayo Jr;Eric D W.Stab and puncture characterization of thermoplastic-impregnated aramid fab- ric[J].International Journal of Impact Engineering,2009(36):1095-1105. |
| [7] | Keith M K;John E K;Young S L .Yarn pull-out as a mechanism for dissipation of ballistic impact energy in Kevlar KM-2 fabric[J].Textile Research Journal,2004,74(11):939-948. |
| [8] | 席时平,崔贵德,陈南梁.压延类柔性复合材料的抗撕裂性能研究[J].产业用纺织品,2005(12):17-19. |
| [9] | GA68-2008.警用防刺服[S].北京:中国标准出版社,2008. |
| [10] | 陈利,张一帆,孙绯,孙颖,李艳亮,唐邦铭,梁子青.预定型平纹织物的剪切模型[J].复合材料学报,2010(02):154-160. |
| [11] | 方心灵,刘胜,左向春,刘腾龙,张艳朋.树脂基体对芳纶材料防刺性能的影响[J].合成纤维,2009(07):45-47. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%