研究了含15wt%Ce的Fe-Ce合金在600～800℃、H2-H2S气氛中的硫化行为,其硫的分压为10-3Pa.结果表明,Fe-15Ce合金的腐蚀速度比纯Fe慢,但比纯Ce快得多,随温度升高其腐蚀速度加快.该合金硫化后形成复杂的腐蚀产物膜,最外层为纯Fe的硫化物层,其下为Ce的硫化物与Fe的硫化物的混合物层;内层为Ce的内硫化区,与之相邻的基体金属层中没有贫Ce现象发生.Ce不能从合金的腐蚀区中向外扩散,而是在腐蚀区内原位地形成Ce的硫化物与Fe的硫化物的混合物.与纯Fe相比,尽管Fe-Ce合金的腐蚀速
The corrosion behavior of Fe Ce alloy containing approximately 15 wt% cerium has been studied at 600～800℃ in H2 H2S atmospheres with a sulfur pressure of 10 3 Pa. The results showed that the alloy was sulfidized more slowly than pure Fe, but more rap
参考文献
| [1] | MrowecS,PrzybylskiK．Hightemp．Mater．Proc．,1984,6:12CarterRV,DouglasDL,GesmundoF．Oxid．Met．,1989,31:3413NiuY,GesmundoF,VianiF．Coros．Sci．,1994,36:8534RaoCNR,PisharodyKPR．ProgresinSolidStateChemistry,McCaldinJO,SomorjaiGEds．,PergamonPress,NewYork,1975,Vol．X,2075GesmundoF,VianiF,NiuY．Oxid．Met．,1994,42:4096GesmundoF,VianiF,NiuY．Oxid．Met．,1996,45:517GesmundoF,VianiF,NiuY,DouglasDL．Oxid．Met．,1994,42:465v |