热塑性聚合物经受稳定的银纹微纤拉伸时,银纹区的迅速增厚将会迅速地引起局部绝热升温现象.预测裂尖银纹的热力学分析可以预测结晶热塑性高聚物冲击断裂阻抗.热反内聚模型用来模拟冲击拉伸过程银纹寿命或反内聚时间.文中报道了一种新型的全切痕蠕变测试法可以在银纹增厚速率高达2m/s时测量平面银纹层的内聚力,在快速拉伸条件下高密度聚乙烯的内聚力和银纹寿命被测量,测试的结果与数值模型的预测结果是相一致的.
参考文献
| [1] | DUGDALE D S .[J].Journal of the Mechanics and Physics of Solids,1960,8:100. |
| [2] | BARENBLATT G I .[J].Advances in applied mechanic,1962,7:55-129. |
| [3] | WILLIAMS J G.Fracture mechanics of polymers[M].Ellis Horwood,Chiehester UK,1987 |
| [4] | LEEVERSPS .[J].International Journal of Fracture,1995,73:109-127. |
| [5] | LEEVERS P S;MORGAN R .[J].Journal of Engineering Fracture Mechanics,1995,52(06):999-1014. |
| [6] | RAGER A .[D].University of London,2003. |
| [7] | Lagaron JM.;Rose LJ.;Kip BJ.;Capaccio C. .Craze morphology and molecular orientation in the slow crack growth failure of polyethylene[J].Journal of Applied Polymer Science,2000(2):283-296. |
| [8] | LEEVERS P S;HAZRA S;HILLMANSEN S .[J].Plastics,Rubber and Composites,2000,29(09):460-467. |
| [9] | Wang L .Thermal de-cohesion model for time of craze failure in cohesive zone[J].Theoretical and Applied Fracture Mechanics,2004(1):75-87. |
| [10] | Fleissner M. .Experience with a full notch creep test in determining the stress crack performance of polyethylenes[J].Polymer engineering and science,1998(2):330-340. |
| [11] | Duan DM.;Williams JG. .Craze testing for tough polyethylene[J].Journal of Materials Science,1998(3):625-638. |
| [12] | Pandya KC.;Williams JG. .Measurement of cohesive zone parameters in tough polyethylene[J].Polymer engineering and science,2000(8):1765-1776. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%