采用异速异步轧制技术,对翼缘板钢分别进行累计九道次冷轧,用光学显微镜、电子扫描显微镜观察轧件的显微组织.结果表明:在相同的压下量下,随着异速比增大,晶粒长度和高度的比值也增大,用晶粒长高比值可以在一定程度上反映异步轧制对轧件所受附加剪切变形影响关系.对冷轧后的轧件进行了拉伸和退火实验,结果表明:随着异速比增大,抗拉强度增加,晶粒平均直径变小,异步轧制与同步轧制相比应变储能更高,可以产生更多的位错和亚晶.
参考文献
| [1] | 罗德兴,张海滨,陈其安.不对称轧制时晶粒细化的研究[J].钢铁,2005(03):59-61. |
| [2] | Iwahashi Y;horita z et al.An investigation of microstruetural evolution during equal-channel angular pressing[J].Acta Materialia,1997,45(17):4733-4741. |
| [3] | Seong-Hee Lee;Tetsuo Sakai;Yoshihiro Saito;Hiroshi Utsunomiya;Nobuhiro Tsuji .Strengthening of sheath-rolled aluminum based MMC by the ARB process[J].Materials transactions,1999(12):1422-1428. |
| [4] | 冯淦,石连捷,吕坚,卢柯.低碳钢超声喷丸表面纳米化的研究[J].金属学报,2000(03):300-303. |
| [5] | 高秀华,齐克敏,邱春林.硅钢极薄带三次再结晶退火过程中的组织演化[J].材料热处理学报,2006(04):91-94. |
| [6] | Cui Q.;Ohori K. .Grain refinement of high purity aluminium by asymmetric rolling[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2000(10):1095-1101. |
| [7] | Jin H;Lloyd DJ .The reduction of planar anisotropy by texture modification through asymmetric rolling and annealing in AA5754[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):358-367. |
| [8] | Jin H;Lloyd D J .The tesile response of a fine-grained AA5754 alloy produced by asymmetric roiling and annealing[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2004,35(03):997-1006. |
| [9] | 张贵杰,李海英,宋卓霞,陈川.异步轧制条件下高锰钢的显微组织与加工硬化机制[J].材料热处理学报,2009(05):115-118. |
| [10] | 张正贵,刘沿东,王福.退火时间对异步轧制无取向硅钢再结晶织构与磁性的影响[J].材料热处理学报,2010(03):69-72. |
| [11] | 王廷溥;齐克敏.金属塑性加工学[M].北京:冶金工业出版社,2000:86-87. |
| [12] | 刘刚 .异步轧制取向硅钢的研究[D].沈阳:东北大学,1997. |
| [13] | 左方青 .纯铝异步轧制剪切形变直接观察及组织性能研究[D].上海交通大学,2008. |
| [14] | 康永林;傅杰.薄板坯连铸连轧钢的组织性能控制[M].北京:冶金工业出版社,2006:374-375. |
| [15] | 钟群鹏;赵子华.断口学[M].北京:高等教育出版社,2006:154-156. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%