为了了解化学组成对电解二氧化锰(EMD)电化学行为的影响,分析了三种商品 EMD的组成,它们分别为Mn0.8814+Mn0.0443+O1.6552-(OH)0.345-、Mn0.8804+Mn0.0483+O1.6662-(OH)0.334-和 Mn0.8794+Mn0.0543+O1.6772-(OH)0.322-, X射线衍射表明晶型为γ-MnO2.通过循环伏安、恒流放电、 电位-时间关系等实验研究其电化学行为,结果表明,EMD中结合水含量(即阳离子空位数) 增加时,样品开路电压升高、放电容量增大、第1电子还原的峰电位正移.
Three electrolytic manganese dioxide (EMD) samples were characterized by XRD and chemical analyses.
Their electrochemical performances were studied by cyclic voltametry, constant-current discharge, and choronopotentiometry. The results show that the
three samples have the same structure, γ-MnO_2, but their combined water contents are different. The chemical compositions of the three samples
can be formulated as A: Mn4+0.881Mn3+0.044O2-1.655(OH)-0.345, B: Mn4+0.880Mn3+0.048O2-1.666(OH)_0.334 and C:
Mn4+0.879Mn3+0.054O2-1.677(OH)-0.322. The electrochemical performances are influenced by the combined water contents,
which are related to the number of cation-vacancy in the samples. The open circuit potential, the discharge capacity and the peak potential of one
electron reduction increase with the increase of the combined water contents in the samples.
参考文献
| [1] | 夏熙. 电池, 1999, 29 (5): 209--216. [2] 张碧泉, 卢兆忠. 高等学校化学学报, 1995, 16 (6): 961--963. [3] Ruetschi P. J Electrochem Soc, 1984, 131 (12): 2737--2744. [4] 李伟善, 吴丽珊, 江琳才. 电池, 1989, 19 (1): 31--35. [5] Li W S, Jiang L C, Xie G Y, et al. J Power Sources, 1996, 58: 235--237. [6] Li W S, Jiang L C, Huang Z T. J Power Sources, 1997, 69: 81--87. [7] Abbas H, Nasser S A. J Power Sources, 1996, 58: 15--21. [8] 马子川, 谢亚勃, 张雪荣. 河北师范大学学报(自然科学版), 2001, 25 (1): 83--85. [9] 梁乐忠. 电池, 1996, 26 (1): 24--25. [10] 王力臻, 项民, 谷书华, 等. 电池, 1999, 29 (4): 157--160. [11] Ruetschi P. J Electrochem Soc, 1988, 135 (11): 2657--2663. [12] Ruetschi P, Gionvanoli R. J Electrochem Soc, 1988, 135 (11): 2663--2669. [13] Rateuville Y, Wu W L, Lincot D, et al. J Electrochem Soc, 1999, 146 (9): 3161--3167. [14] Korzawa A, Powers R A. J Electrochem Soc, 1966, 113 (9): 870--878. |