对氢电弧等离子体法制备的纳米NiCe合金粒子中稀土元素Ce的作用进行了分析,由EDS及XRD结果可以看出纳米粒子表面壳层富集Ce且与Ni形成CeNi合金相,为新的表面活性中心;同时由DSC结果发现,Ce的加入使nano-NiCe粒子的热稳定性比nano-Ni粒子提高近90℃.因此,Ce的加入使得纳米NiCe粒子具有高的催化活性和稳定性.
参考文献
| [1] | Taylor K C.Catalysis Science and Technology[M].Springer-Verlag,1984 |
| [2] | Schlatter J C;Mitchell P J .[J].Industrial & Engineering Chemistry Process Design and Development,1980,19:288. |
| [3] | Herz R K;Sell J A .[J].Journal of Catalysis,1985,94:166. |
| [4] | Chen K Z;Zhang Z K;Cui Z L et al.[J].Nano-Structured Materials,1997,8(02):205. |
| [5] | Chen K Z;Zhang Z K;Cui Z L et al.[J].Journal of Materials Science and Technology,1997,13(03):215. |
| [6] | 左东华;张志琨;崔作林 等.[J].催化学报,1996,17(02):166. |
| [7] | Cui Z L;Zhang Z K .[J].Nanostructured Materials,1996,7(07):355. |
| [8] | 孟庆珍;胡鼎文;程泉寿.无机化学[M].北京:北京师范大学出版社,1988 |
| [9] | Solymosi F;Pasztor M;Rakhely G .[J].Journal of Catalysis,1988,110:413. |
| [10] | Summers J C;Ausen SA .[J].Journal of Catalysis,1979,58:131. |
| [11] | Yan Oian-Gu;Yu Zuo-Long .[J].Journal of Natural Gas Chemistry,1997,6(02):93. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%