研究了高温时效对标准和改型Thermo-Span合金组织和持久性能的影响,在650℃时效1000 h,标准合金的晶内与晶界Laves析出相均发生了粗化,而改型合金的析出相形貌没有改变,当时效温度增高到680℃时,标准合金在时效500 h时,合金的析出相已经发生了严重的粗化,Laves相的形态由圆粒状变成条状,而改型合金的析出相没有变化,当时效到1000 h后,标准合金析出相已经完全粗化,析出相几乎布满了整个晶内,而改型合金晶界只有少量析出相开始发生粗化,经650 ℃时效1000 h后,改型合金具有较好的组织热稳定性,合金650℃/600 MPa的持久性能比标准合金高109 h.
参考文献
| [1] | 邓波,韩光炜,冯涤.低膨胀高温合金的发展及在航空航天业的应用[J].航空材料学报,2003(z1):244-249. |
| [2] | Sato K;Ohno T .Development of low thermal expansion superalloys[J].Journal of Materials Engineering and Performance,1993,2(04):511-516. |
| [3] | Tundermann J H .Development of Inconel alloy 783,a low thermal expansion,crack growth resistanct superalloys[J].Acta Metallurgica Sinica (English Letters),1996,9(06):503-507. |
| [4] | Hedk K A;Smith D F;Smith J S.The physical metallurgy of a silicon-containg low expansion superalloy[A].,1988:151-160. |
| [5] | Wanner E A;Daniel D A.Development of a new controlled Thermal Expansion superalloy with improved oxidation resistance[A].,1992:237-246. |
| [6] | Ecer G M;Meier G H .Oxidation of parabolic reaction rate constants[J].Oxidation of Metals,1987,27:1787-1803. |
| [7] | 孙雅茹,于连旭,孙文儒,孙晓峰,郭守仁,胡壮麒.冷却速度对Thermo-Span合金组织和持久性能的影响[J].材料热处理学报,2010(03):39-42. |
| [8] | 胡轶嵩,于连旭,杨连忠,李晓欣,王志宏.Thermo-Span合金在650℃长期时效稳定性[J].材料热处理学报,2013(08):55-59. |
| [9] | Ladna B;Birnbaum H K .Surface and grain boundary segregation of sulfur and boron in nickel[J].ACTA METALLURGICA,1988,36(03):745-755. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%