利用硅烷偶联剂KH-550对不同形貌ZrWMoO8进行表面改性,通过红外光谱(FT-IR)、接触角测试仪、扫描电镜(SEM)、X射线衍射(XRD)分析改性后ZrWMoO8的性能变化.结果表明,硅烷偶联剂改性后ZrWMoO8的晶体结构没有发生变化,但其接触角变大,疏水性增强,微粉团聚现象减少,分散性增强.
参考文献
| [1] | Evans J S O;Mary T A;Sleight A W .Negative thermal expansion materials[J].Physica B:Condensed Matter,1997,241:311-316. |
| [2] | Mary T A;Evans J S O;Vogt T et al.Negative thermal expansion from 0.3 to 1050 Kelvin in ZrW2O8[J].SCIENCE,1996,272(5258):90-92. |
| [3] | Evans JSO;Jorgensen JD;Short S .Compressibility, Phase Transitions, and Oxygen Migration in Zirconium Tungstate, ZrW2O8[J].Science,1997(5296):61-65. |
| [4] | Arthur W.Sleight .Isotropic negative thermal expansion[J].Annual review of materials research,1998(0):29-43. |
| [5] | Closmann C.;Haygarth JC.;Sleight AW. .Low-temperature synthesis of ZrW2O8 and Mo-substituted ZrW2O8[J].International Journal of Quantum Chemistry,1998(2):424-426. |
| [6] | Pryde A K A;Hammonds K D;Dove M T et al.Origin of the negative thermal expansion in ZrW2O8 and ZrV2O7[J].Journal of Physics:Condensed Matter,1996,8(50):10973. |
| [7] | 杨娟,刘芹芹,程晓农,孙秀娟.ZrO2/β-ZrWMoO8可控热膨胀复合材料的制备[J].江苏大学学报（自然科学版）,2010(06):670-673. |
| [8] | 严学华,程晓农,徐桂芳,王春生,李炳云.α-ZrW2O8/Cu复合材料的制备、微观结构和致密度[J].江苏大学学报（自然科学版）,2009(02):152-155. |
| [9] | 来育梅,王伟,王晓东,黄培.热塑性聚酰亚胺的热膨胀系数研究[J].塑料工业,2005(10):41-43. |
| [10] | Sullivan, LM;Lukehart, CM .Zirconium tungstate (ZrW2O8)/polyimide nanocomposites exhibiting reduced coefficient of thermal expansion[J].Chemistry of Materials,2005(8):2136-2141. |
| [11] | Juan Yang,Yongsen Yang,Qinqin Liu,Guifang Xu,Xiaonong Cheng.Preparation of Negative Thermal Expansion ZrW2O8 Powders and Its Application in Polyimide/ZrW2O8 Composites[J].材料科学技术学报（英文版）,2010(07):665-668. |
| [12] | 廖俊,陈圣云,康宇峰,张先亮.硅烷偶联剂及其在复合材料中的应用[J].化工新型材料,2001(09):26-28. |
| [13] | 沈玺,高雅男,徐政.硅烷偶联剂的研究与应用[J].上海生物医学工程,2006(01):14-17. |
| [14] | 俞振海,卢晗锋,梁锦,陈银飞.硅烷偶联剂对氢氧化镁表面改性及其在聚丙烯中的应用[J].无机盐工业,2010(02):12-14,27. |
| [15] | 薛茹君,吴玉程.硅烷偶联剂表面修饰纳米氧化铝[J].应用化学,2007(11):1236-1239. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%